Abstract:Despite significant efforts to develop ultra-high temperature ceramics, the phase stability together with high hardness and oxidation resistance remains to be addressed in ZrB2-SiC based ceramics. ZrB2-20 vol% SiC (ZS20) ceramics with varying amounts of Si3N4 (2.5, 5 and 10 vol%) were processed by multi stage Spark Plasma Sintering (SPS) over a range of temperature (1800–1900 °C) for 3 min under 50 MPa. All the ZS20-Si3N4 composites could be densified to more than 98% theoretical density (ρth) after SPS at 1900 °C. The XRD, SEM-EDS analysis of the ZS20-Si3N4 composites revealed the presence of reaction product phases (ZrO2, BN, ZrN) along with SiC and ZrB2 major phases. Sintering reactions were proposed to explain the existence of such new phases and extinction of Si3N4. Thermo-Calc software was also used to further confirm the formation of these new phases in the ZS20-Si3N4 samples. The hardness of ZS20-Si3N4 composites varied between 25.50 and 30.56 GPa, in particular, ZrB2-20 vol% SiC-5vol% Si3N4 measured with the maximum hardness. In fact, it is the highest ever reported hardness for the ZrB2 composites. Considering oxidation resistance, the weight gain of ZrB2-20 vol%SiC composites decreased (from 13.84 to 9.84 mg/cm2) and oxide layer thickness increased (64–128 μm) after oxidation at 1500 °C for 10 h in air. The cross sectional microstructure of oxidized ZS20-Si3N4 composites consists of thick dense outer layer of SiO2, intermediate (ZrO2-SiO2) layer and unreacted bulk. The formation of dense SiO2 layer and absence of SiC depleted layer from the oxidized samples are signatures of improved oxidation resistance of Si3N4 reinforced ZrB2-20 vol% SiC.

High Entropy Boride-SiC Composite: Synthesis, Characterization and Thermo-oxidative behaviour

Effect of SiC on Microstructure, Phase Evolution, and Mechanical Properties of Spark-Plasma-Sintered High-Entropy Ceramic Composite

High-Entropy Diborides—Silicon Carbide Composites by Reactive and Non-Reactive Spark Plasma Sintering: A Comparative Study

Optimal preparation of high-entropy boride-silicon carbide ceramics

Synthesis and electromagnetic wave absorbing properties of high-entropy metal diboride-silicon carbide composite powders

Exceptional hardness and thermal properties of SiC/(Hf,Ta)C(N)/ (B)C ceramic composites derived from single‐source precursor

Reactive sintered dense carbon fiber reinforced high‐entropy boride composite using high‐entropy silicide as reactant

Low-temperature densification of high entropy diboride based composites with fine grains and excellent mechanical properties

Mechanical properties of hot-pressed high-entropy diboride-based ceramics

The role of carbon addition on properties of boron carbide- silicon carbide composites

Influence of Silicon Addition on the Sintering Behavior and Mechanical Properties of Boron Carbide by SPS Process

Effect of the amount of SiC particles on the microstructure, mechanical and wear properties of FeMnCoCr high entropy alloy composites

B4C-SiC composites with tuneable mechanical properties: Role of Al2O3 - Y2O3 sintering additives

Ultra-fast high-temperature synthesis and densification of high-entropy diborides and diboride-carbide ceramics

Phase stability, hardness and oxidation behaviour of spark plasma sintered ZrB2-SiC-Si3N4 composites

Effect of SiC Content on Mechanical and Tribological Properties of Al2024-SiC Composites

Synthesis and Thermal Oxidation Resistance of Boron-Rich Boron-Carbide Material

Microstructure, Mechanical and Tribological Properties of High-Entropy Carbide (MoNbTaTiV)C5

Rapid liquid phase-assisted ultrahigh-temperature sintering of high-entropy ceramic composites

Dense and pure high-entropy metal diboride ceramics sintered from self-synthesized powders via boro/carbothermal reduction approach

Silicon oxycarbide composites reinforced with silicon nitride and in situ formed silicon carbide.