Abstract:Electrochromic devices are applied extensively to camouflages, smart windows, heat insulation layers, and automobile rearview mirrors, etc. The amorphous WO 3 is a very attractive electrochromic material, whereas it suffers from degradation of optical modulation and reversibility on ion exchange owing to those deep trapped ions with irreversible reaction behavior. Herein, we designed and, by using magnetron sputtering, prepared a composite film with TiO 2 /WO 3 /TiO 2 double heterojunctions, which is capable of eliminating the deep trapped ions by itself under ultraviolet light (UV) assistance. The electrochromic device based on this composite film, after being recovery by short-time UV irradiation, can maintain a high transmission modulation of 94.72% after 7000 cycles of the voltammetry measurement. This feature allows the device to maintain its initial electrochromic performance after prolonged use. Moreover, the double heterojunction structure can reduce colouring time and enormously improve the colouration efficiency (CE) of electrochromic devices. Experimental research shows that when the thickness of the bottom and upper TiO 2 layer of the WO 3 film was 145.5 nm and 97.0 nm, respectively, the CE of electrochromic devices reached a perfectly high value (479.3 cm 2 /C), being much higher than that of WO 3 devices (69.5 cm 2 /C). Functions of the TiO 2 /WO 3 /TiO 2 double heterojunction in electrochromic device were investigated by combining theoretical analysis and experiment validation, and these results provide a general framework for developing and designing superior electrochromic materials and devices.

Preparation and Electrochromism of Amorphous Bi-doped TiO2 Film for Aqueous-Based Electrochromic Device

Electrochromism of titanium oxide thin films

Building Architecture of TiO2 Nanocrystals Embedded in Amorphous WO3 Films with Improved Electrochromic Properties

A facile synthesis of porous amorphous/crystalline TiO2 hybrids for enhanced electrochromic performances

Enhanced Electrochromic Properties of Donor–acceptor Polymers Via TiO2 Composite

Improved electrochromic device based on mesoporous TiO2 and NiO films

Improvement of Electrochromic Performance by Embedding ITO Nanocrystals in Amorphous WO3 Film

Citric Acid Induced W18O49 Electrochromic Films with Enhanced Optical Modulation

Construction of TiO2/WO3/TiO2 double heterojunction films for excellent electrochromic performance

Investigation on the Properties and Mechanism of W-Doped TiO<sub>2</sub> Electrochromic Films Deposited by Cosputtering

Dip-Coating Process Engineering and Performance Optimization for Three-State Electrochromic Devices

Electrochromic TiO2 Films by a Facile Solvothermal Process: Effect of Ethanol Content on Growth and Performance

Study on the Structure and Electrochromism of WO<sub>3</sub> and Ti-Doped WO<sub>3</sub> Films

Electrochromic Performance Fading and Restoration in Amorphous TiO2 Thin Films

Synthesis of Nitrogen-Doped Carbon Embedded TiO2 Films for Electrochromic Energy Storage Application

Effects of Ti-doping amount and annealing temperature on electrochromic performance of sol-gel derived WO3

Eradicating Β-Trap Induced Bleached-State Degradation in Amorphous TiO2 Electrochromic Films

Enhancement of electrochromic properties using nanostructured amorphous tungsten trioxide thin films

Amorphous bismuth and GO co-doped WO3 electrochromic film with fast-switching time and long-term stability

Preparation and Electrochromic Study of Ce3+ Doped TiO2 Thin Films

Electrochromic Performance Fading and Restoration in Amorphous TiO<sub>2</sub> Thin Films