Abstract:Black silicon materials were obtained by irradiation with ns laser pulses in different ambient atmospheres. The surface morphology, optical properties, and electrical properties of the black silicon were investigated after the ablation by ns laser pulses. Slab-like structures and boundaries were formed on the surface of black silicon fabricated in sulfur hexafluoride (SF 6 ), argon (Ar), and vacuum. In addition, a micrometer-sized sphere was observed at the tip of the slab-like structure, which was not obvious for the black silicon prepared in oxygen (O 2 ), nitrogen (N 2 ), and air. The infrared absorption of all the black silicon materials was enhanced. For the two samples fabricated in SF 6 and Ar, the infrared absorptance was approximately 50% at 1500 nm. A post-thermal annealing process decreased the infrared absorptance of all the black silicon materials except for that prepared in SF 6 . The sheet resistance of the black silicon was reduced by the ns laser irradiation process, and thermal annealing further decreased the sheet resistance of all the samples except for the one fabricated in SF 6 . After annealing at 875 K, the sheet carrier density of the black silicon fabricated in an Ar atmosphere and vacuum was approximately 10 13 cm −2 , which was approximately three orders of magnitude larger than that of the silicon substrate (10 10 cm −2 ). The large difference in carrier density between the black silicon layer and substrate is beneficial for establishing contact junctions and for application in infrared photodetection.

Reflective Properties of Black Silicon in a Wide Spectral Range

Optical properties of black silicon prepared by wet etching

Wide‐Range Wavelength Light Scattering from Black Silicon Layers: Profits for Perovskite/Si Tandem Solar Cells

Wide-band “black Silicon” Based on Porous Silicon

A Theoretical Study on the Optical Properties of Black Silicon

Advances in Fabrication and Application of Black Silicon

Black Silicon as Anti-Reflective Structure for Infrared Imaging Applications

Ultralow Broadband Reflectivity in Black Silicon Via Synergy Between Hierarchical Texture and Specific‐Size Au Nanoparticles

Properties of Black Silicon Layers Fabricated by Different Techniques for Solar Cell Applications

Anti-Reflectance Optimization of Secondary Nanostructured Black Silicon Grown on Micro-Structured Arrays.

Comparison of Different Etching Methods on the Morphology and Semiconductor Characters of Black Silicon

Review Application of Nanostructured Black Silicon

Effect of thermal annealing on the structural and optical properties of black silicon

Study on the Optical Characteristic of "black Silicon" Antireflection Coating Prepared by Plasma Immersion Ion Implantation

Fabrication of Black Silicon Materials by Wet Etching and Characterization

Black silicon for near-infrared and ultraviolet photodetection: A review

Black Silicon with Order-Disordered Structures for Enhanced Light Trapping and Photothermic Conversion

Recent Progress of Black Silicon: From Fabrications to Applications

Properties investigation of crystalline silicon surface irradiated by nanosecond laser pulses in different background atmospheres

Black Silicon Surface-Enhanced Raman Spectroscopy Biosensors: Current Advances and Prospects

Enhanced near-infrared absorber: two-step fabricated structured black silicon and its device application