Abstract:Titanium matrix composites reinforced with titanium boride (TiB) and titanium carbide (TiC) were fabricated in situ via selective laser melting (SLM). Varying contents of boron carbide (B4C) from 0 to 5 wt% were added to pure Ti to prepare blended powders for SLM. The influence of the B4C content on the printability, microstructure and mechanical properties of SLM-printed (TiB + TiC)/Ti composites was studied. The relative densities of all the fabricated composites were greater than 97.8 %; an increase in the B4C content resulted in a decrease in their relative density. The microstructure of the composites varied from a lath-shaped structure (0 wt%) to a dendritic structure (1 wt%) and to a cellular + dendritic structure (2–5 wt%), which was determined by the change of thermal convection within melt pools. Both the dendritic and cellular structures were arranged by coalescent clusters composed of TiB whiskers and TiC particles, while the clusters were formed through a self-joining behavior of the TiB whiskers that were mechanically locked with the TiC particles. The composites with the addition of 1 wt% B4C exhibited the highest ultimate tensile strength of 946 MPa, yield strength of 762 MPa and elastic modulus of 128 GPa, which were 62.4 %, 49.2 % and 15.3 % higher than those of the Ti matrix, respectively. The remarkable enhancement in the mechanical strengths was attributed to the synergistic effect of dispersion strengthening and grain refinement strengthening. The (TiB + TiC)/Ti composites fabricated in situ by SLM with an optimized material formulation not only ensured comparable mechanical properties to those of their counterparts manufactured by conventional processes but also demonstrated the potential in manufacturing complex and/or customized parts with design freedom for industrial applications.

Microstructure and Properties of Ti/(TiB+TiC)composites Prepared by Low-Cost TiH2 Powders

Microstructure and Wear-resistant Properties of in situ TiB-TiC Reinforced Titanium Matrix Composites by Laser Deposition Manufacturing

Effect of TiB_2 content on microstructure and mechanical properties of in-situ fabricated TiB_2/B_4C composites

PREPARATION AND PROPERTIES OF TiB2/TiAl COMPOSITE SHEETS WITH LAYERED STRUCTURE

In situ (TiBw+TiCp)/Ti6Al4V composites with a network reinforcement distribution

Microstructure and mechanical properties of in-situ hybrid reinforced (TiB+TiC)/Ti composites prepared by laser powder bed fusion

Microstructures and tensile properties of low-cost TiBw/Ti–6Al–4V composites by vacuum reactive hot pressing

MICROSTRUCTURE AND MECHANICAL PROPERTIES OF IN-SITU SYNTHESIZED TITANIUM MATRIX COMPOSITES PREPARED BY POWDER METALLURGY

Microstructural characterization and mechanical properties of (TiC+TiB)/TA15 composites prepared by an in-situ synthesis method

Microstructure and Mechanical Properties of Cu Matrix Composites Reinforced by TiB2/TiN Ceramic Reinforcements

Microstructure and properties of TiCx/TC4 composites with a quasi-network structure prepared by the decomposition of the Ti2AlC precursor

Microstructure and Mechanical Properties of Ti-TiH2 Based Matrix Composites Reinforced with xTiB2 Particles Processed by Powder Metallurgy

Achieving high strength and superior wear‐resistant properties in TiH2 matrix reinforced with graphene nanoplates

Mechanical property and microstructure of in-situ TiB/Ti composites via vacuum sintering and hot rolling

Effect of TiC content on the microstructure and mechanical properties of Ti-30Mo-xTiC composites

Microstructure of In-Situ Synthesized (tib+tic)/ti Composites Prepared by Hot-pressing

Microstructure and superior mechanical property of in situ (TiBw + TiCp)/Ti composites with laminated structure

B4C‒TiB2 composite with modified microstructure and enhanced properties from optimal size coupling of raw powders

Microstructure and mechanical properties of (TiB+TiC)/Ti composites fabricated in situ via selective laser melting of Ti and B4C powders

Enhancement mechanical properties of in-situ preparated B4C-based composites with small amount of (Ti3SiC2+Si)

Microstructure and Mechanical Properties of TiN–TiB2–hBN Composites Fabricated by Reactive Hot Pressing Using TiN–B Mixture