Abstract:Ti-6.5Al-2Zr-1Mo-1V/TiB metal matrix composites with 3 wt.% of TiB2 were obtained using vacuum arc melting and spark plasma sintering methods and compared with an unreinforced Ti-6.5Al-2Zr-1Mo-1V alloy. The microstructures of the unreinforced Ti6.5Al-2Zr-1Mo-1V alloy in the as-cast and as-sintered conditions were quite typical and consisted of colonies of α-lamellae embedded in the β matrix. The microstructure of the as-cast Ti-6.5Al-2Zr-1Mo-1V/TiB composite composed of TiB fibers randomly distributed within the two-phase α/β matrix, while the as-sintered composite had a network-like microstructure, in which areas of the two-phase α/β matrix were delineated by walls of TiB fibers. At room temperature, the yield strength of the as-cast and as-sintered Ti-6.5Al-2Zr-1Mo-1V alloy were 800 and 915 MPa, respectively, with a plasticity of 18% in both conditions. The addition of TiB fibers contributed to a ~40 and 50% strength increment, with values of 1100 and 1370 MPa for the as-cast and as-sintered composites, respectively. In the as-sintered composite, the strengthening effect reduced at 400 °C and almost disappeared at elevated temperatures of 800–950 °C. The as-cast composite showed much higher strength during warm and hot deformation—at 800–950 °C, the yield strength of the as-cast composite was 50% higher compared to the Ti-6.5Al-2Zr-1Mo-1V unreinforced alloy. A higher rate and degree of globularization were established for the as-cast composite compared to the unreinforced alloy. For the as-sintered composite, a noticeably lower rate and degree of globularization was shown. During hot compression of the as-cast composite, TiB fibers reoriented towards the metal flow direction, while the network microstructure formed in the as-sintered composite transformed into clusters of borides unevenly distributed within the matrix. Based on the obtained results, the apparent activation energy of plastic deformation was calculated, and the operating deformation mechanisms were discussed both for the as-cast and as-sintered composites. The Arrhenius flow stress model and the dynamic material model were used to evaluate the deformation behavior of composites beyond the experimentally studied temperatures and strain rates.

Microstructures and tensile properties of low-cost TiBw/Ti–6Al–4V composites by vacuum reactive hot pressing

In Situ TiBw/Ti–6Al–4V Composites with Novel Reinforcement Architecture Fabricated by Reaction Hot Pressing

High Temperature Tensile Properties of in Situ TiBw/Ti6Al4V Composites with a Novel Network Reinforcement Architecture

In situ (TiBw+TiCp)/Ti6Al4V composites with a network reinforcement distribution

Room temperature tensile fracture characteristics of in situ TiBw/Ti6Al4V composites with a quasi-continuous network architecture

IN SITU TiBW/Ti COMPOSITES WITH A NOVEL QUASI- CONTINUOUS NETWORK REINFORCEMENT ARCHITECTURE

Microstructures and mechanical properties of (TiBw+Ti 5 Si 3 )/TC11 composites fabricated by hot isostatic pressing and subjected to 2D forging

Analysis of the Microstructure and Mechanical Properties of TiBw/Ti-6Al-4V Ti Matrix Composite Joint Fabricated Using TiCuNiZr Amorphous Brazing Filler Metal

Mechanical property and microstructure of in-situ TiB/Ti composites via vacuum sintering and hot rolling

Thermomechanical Processing of a Near-α Ti Matrix Composite Reinforced by TiBw

Enhancing strength-ductility synergy in nano-sized TiB 2 /Al composite via rapid solidification and thermo-mechanical processing

Microstructure, densification and mechanical properties of in situ TiBw/Ti2AlNb composites fabricated by spark plasma sintering

Densification behavior, mechanical and electrical properties of in-situ TiB 2p /Cu composite powder via vacuum hot pressing

Nearly dense Ti–6Al–4V/TiB composites manufactured via hydrogen assisted BEPM

Network-Strengthened Ti-6Al-4V/(TiC+TiB) Composites: Powder Metallurgy Processing and Enhanced Tensile Properties at Elevated Temperatures

Achieving ultra-high strength in TiB/metastable-β composites via short-process technology

New insights into the microstructural evolution and properties of (TiB+TiC)/Ti–6Al–4V composite via laser directed energy deposition using B 4 C nanoparticles

Microstructure Evolution and Mechanical Behavior of TiB-Reinforced Ti-6.5Al-2Zr-1Mo-1V Matrix Composites Obtained by Vacuum Arc Melting and Spark Plasma Sintering

Microstructure and mechanical properties of GNPs and in-situ TiB hybrid reinforced Ti–6Al–4V matrix composites with 3D network architecture

Enhancing microstructure refinement and strengthening efficiency of TiBw/near α-Ti composites by combining solid-solution treatment with hot processing

Hot Deformation Behavior and Workability of In-Situ TiB2/7050Al Composites Fabricated by Powder Metallurgy