Abstract:The fatigue performance of titanium (Ti) alloys fabricated by laser powder bed fusion (LPBF) is a crucial factor influencing the structural safety in service. The high-cycle fatigue (HCF) of LPBF Ti-6.5Al-3.5Mo-1.5Zr-0.3Si alloy at the room temperature and 500 degrees C was tested. Compared with the room-temperature samples, the fatigue strength of fatigue samples tested at 500 degrees C is reduced by about 55.8 % after 106 fatigue cycles. Crack initiation on the surface is mainly related to fatigue after fewer cycles under high stress, while interior cracks initiate after a longer fatigue life under low stress. Electron back scattering diffraction (EBSD) was adopted to characterize the orientations of grains on the crack propagation paths and the activated slip systems. All prismatic oriented grains were found to activate prismatic slip systems, the activation of which achieves symmetric slips surrounding crack tips, forms ductile striations, and increases energy absorption during crack propagation. These characteristics are conducive to improved fatigue performance. About half of the basal oriented grains activate prismatic slip systems. These activated prismatic slip systems not only have a high Schmid factor (SF) but also need to have a high geometrical compatibility factor with slip systems activated by adjacent grains. The residual (3 phase and alpha phase are aligned according to the Burgers orientation relationship (BOR), so the (3 phase does not alter the direction of crack propagation. The results were used to predict the fatigue crack propagation paths in LPBF Ti-6.5Al-3.5Mo-1.5Zr-0.3Si alloy during loading along building and transverse directions were predicted. This, to some extent, provides a basis for comparing fatigue performance of LPBF Ti alloys in different directions.

Damage Accumulation and Its Effect During Thermal- and Stress-Induced Cycling Martensite Transformation of Laser Powder Bed Fused (LPBF) NiTi Alloy

Anisotropy in Microstructural Features and Tensile Performance of Laser Powder Bed Fusion NiTi Alloys

A large compressive recoverable strain induced by heterogeneous microstructure in a Ni50.6Ti49.4 shape memory alloy via laser powder bed fusion and subsequent aging treatment

Leaf-Like Dislocation Substructures And The Decrease Of Martensitic Start Temperatures: A New Explanation For Functional Fatigue During Thermally Induced Martensitic Transformations In Coarse-Grained Ni-Rich Ti-Ni Shape Memory Alloys

Toward additive manufactured crack-free NiTiCu shape memory alloys with low-hysteresis and tailorable phase transition behavior supported by theoretical design

Effect of microstructure on the superelasticity of high-relative-density Ni-rich NiTi alloys fabricated by laser powder bed fusion

Effect of Cyclic Loading on Apparent Young's Modulus and Critical Stress in Nano-Subgrained Superelastic NiTi Shape Memory Alloys

Thermal effects on wear behavior of additively manufactured NiTi shape memory alloys

Cyclic Phase Transformation Behavior of Nanocrystalline NiTi at Microscale

Whole-life transformation ratchetting and fatigue of super-elastic NiTi Alloy under uniaxial stress-controlled cyclic loading

Degradation of the recoverable strain during stress controlled full transformation cycling in NiTi shape memory alloys

Healing cracks in additively manufactured NiTi shape memory alloys

Multiscale Plasticity Behavior and Fatigue Performance of Laser Melting Multi-Layer Nickel-Based Superalloys Upon Heat Treatments

In-situ Synchrotron Diffraction Study of the Localized Phase Transformation and Deformation Behavior in NiTi SMA

Topological optimisation and laser additive manufacturing of force-direction-sensitive NiTi porous structures with large deformation recovery behaviour

Deformation mechanisms of low cycle fatigue of a fourth generation Ni-based single crystal superalloy

Effect of laser scanning speed on the microstructure, phase transformation and mechanical property of NiTi alloys fabricated by LPBF

Influences of Grain Orientation on High-Cycle Fatigue Performance of Laser Powder Bed Fused Ti-6.5Al-3.5Mo-1.5Zr-0.3Si Alloy at Room Temperature and 500 °C

The roles of residual martensite and plastic deformation in thermomechanically coupled functional degradation of nanocrystalline superelastic NiTi alloys

Deformation mechanisms in a TiNi shape memory alloy during cyclic loading

The Effect of Thermal Cycle on Hot Cracking Evolution and Formation Mechanism in Thin Wall, Single Layer, and Cubic Samples of High-Strength Al-Cu-Mg-Mn Alloys Fabricated by Laser Powder Bed Fusion