Abstract:In this work, a ∼220 μm-thick heterogeneous remelted layer is achieved in the coarse-grained AZ41 Mg alloy by the laser surface remelting treatment. Microstructural evolution observations reveal that the remelted heterogeneous layer consists of gradient refined equiaxed α-Mg grains (average grain size from ∼4.6 μm in the bottom to ∼ 60 nm at the surface) and dispersed block-shaped nanoscaled β-Mg17Al12 precipitations (∼22.8 nm), which is obviously different from the favored coarse dendritic or cellular α-Mg grains and lamellar β precipitations during conventional laser processing. The formation of this remelted layer is attributed to constitutional supercooling caused by solute elements and the thermal undercooling generated by the high cooling rates based on optimized processing parameters and liquid nitrogen cooling. The heterogeneous nanostructured remelted layer makes the laser-treated sample has a high hardness of 1.51 GPa, a yield strength of 230.4 MPa and an ultimate tensile strength of 313.7 MPa with a good ductility (12.5%). The laser-treated samples also show the higher fatigue lifetimes in low-cycle as well as high-cycle fatigue tests, which are respectively 2.3 and 18.6 times higher than the original samples. In addition, the laser-treated specimen exhibits a 25% higher fatigue limit compared with the original sample. The synergistic strengthening mechanism including gradient grain refinement and dispersed nanoscaled precipitations are quantitatively discussed to improve strength-ductility synergy and strain hardening capacity in the laser-treated samples. This mechanism could effectively facilitate resisting the initiation and propagation of the fatigue microcracks, which was further validated by the in-situ transmission electron microscope observations. Our results in this study could be further applied for the modification of grain morphology and precipitation distribution for additive manufacturing applications, critical to the development of advanced structural Mg alloys with high service performance in practical engineering environments.

Multiscale Plasticity Behavior and Fatigue Performance of Laser Melting Multi-Layer Nickel-Based Superalloys Upon Heat Treatments

Stress Shielding in Laser Melting Multilayered Nickel-Base Superalloys under Monotonic and Cyclic Loadings

Effects of Heat Treatments on Microstructure and Mechanical Properties of Laser Melting Multi-Layer Materials

Cyclic plasticity modeling and fatigue life assessment of the recasting material of a nickel-based superalloy induced by laser manufacturing

Characterization of the Recasting-Affected Zone in the Nickel-Based Superalloy Upon Single-Pulse Laser Treatment

Shielding Effects on Fatigue and Crack Growth of the Recasting Zone Induced by Laser Manufacturing in a Nickel-Based Superalloy

Microstructural characterization and fatigue performance of the recast material induced by laser manufacturing of a nickel-based superalloy

Experimental Characterization and Strengthening Mechanism of Process-Structure-property of Selective Laser Melted 316 L

In-situ Study of Microstructure and Mechanical Properties of GH3536 Alloy Manufactured by Selective Laser Melting at 750 °C

Deformation Mechanisms of Selective Laser Melted 316l Austenitic Stainless Steel in High Temperature Low Cycle Fatigue

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Multiscale analysis of interior cracking behavior of Ni-based superalloy fabricated by selective laser melting under very-high-cycle-fatigue at high-temperature

Effect of treatment mode on microstructure evolution and mechanical properties of nickel-based superalloy fabricated by selective laser melting

Effects of Thermal Stress on the Formation and Cracking Behavior of Nickel-Based Superalloys by Selective Laser Melting Based on a Coupled Thermo-Mechanical Model

Effects of Recast Layer on Fatigue Performance of Laser-Drilled Holes in Nickel-Based Superalloy

Effect of Warm Laser Shock Peening on the Low-Cycle Fatigue Behavior of DD6 Nickel-Based Single-Crystal Superalloy

Multi-scale experimental investigation on microstructure related subsurface fatigue cracking behavior of selective-laser-melted superalloy at elevated temperature

Superior strength-ductility synergy and fatigue resistance of heterogeneous structured AZ41 Mg alloy by laser surface processing

Effect of elevated temperature on high-cycle and very-high-cycle fatigue properties of Ni-based superalloy manufactured by selective laser melting

Cyclic plasticity and fatigue damage of CrMnFeCoNi high entropy alloy fabricated by laser powder-bed fusion

Thermal behavior and microstructural evolution of additively manufactured Ni-based superalloys via multi-scale simulation