Abstract:Laser drilling is always accompanied by recast layers, micro-cracks, and heat-affected zones, which limit its application in engineering. Due to its unique advantages, such as no heat-affected zones, no residual stresses, and no dependence on the mechanical properties of the materials, electrochemical dissolution has been adopted to remove the laser drilling-induced surface defects. The electrochemical dissolution characteristics and surface evolution of the laser-drilled Ni-based superalloys were studied. The polarization curves and electrochemical impedance spectroscopy (EIS) of the laser-drilled materials and the substrate were measured, indicating that the laser-drilled surface had a smaller corrosion resistance than the original substrate. X-ray photoelectron spectroscopy (XPS) results showed that the laser-drilled surface had a much higher oxygen content than the substrate. Additionally, electric current efficiency curves were obtained to study the anodic dissolution behavior of Ni-based superalloys. An electric current density in the 5–40 A/cm2 range was preferred to enhance the electrochemical dissolution rate. Moreover, the effects of electric current densities and post-processing time on the surface roughness and the recast layer thickness of the laser-processed Ni-based superalloys were investigated using a NaCl and NaNO3 solution electrolyte. The evolution of the surface quality and recast layer thickness were clarified. Furthermore, an anodic dissolution model of the laser-processed surface was established to illustrate the electrochemical post-processing mechanisms. Results revealed that electrochemical dissolution could completely remove the laser drilling-induced surface defects in 20 s using a 12.5 wt.% NaNO3 solution electrolyte and a 40 A/cm2 electric current density. Finally, an electrochemical post-processed surface with surface roughness (Ra) of 1.7 µm and without a recast layer was achieved. Micro holes without recast layers and Ra of 0.69 µm were obtained with high efficiency using laser processing and electrochemical post-processing.

Effects of Recast Layer on Fatigue Performance of Laser-Drilled Holes in Nickel-Based Superalloy

Shielding Effects on Fatigue and Crack Growth of the Recasting Zone Induced by Laser Manufacturing in a Nickel-Based Superalloy

Microstructural characterization and fatigue performance of the recast material induced by laser manufacturing of a nickel-based superalloy

Quantitative Study of High-Frequency Fatigue Hole-Edge Stresses in Nickel-Based Single-Crystal Superalloy

Improving the fatigue property of diffusive film cooling holes in nickel-based single crystal superalloy via ultrashort pulse laser drilling coupled with abrasive flow machining

Multiscale Plasticity Behavior and Fatigue Performance of Laser Melting Multi-Layer Nickel-Based Superalloys Upon Heat Treatments

Cyclic plasticity modeling and fatigue life assessment of the recasting material of a nickel-based superalloy induced by laser manufacturing

Stress Shielding in Laser Melting Multilayered Nickel-Base Superalloys under Monotonic and Cyclic Loadings

Characterization of the Recasting-Affected Zone in the Nickel-Based Superalloy Upon Single-Pulse Laser Treatment

Fatigue performance improvement of laser shock peened hole on powder metallurgy Ni-based superalloy labyrinth disc

Study on anodic dissolution behavior and surface evolution of laser-drilled Ni-based superalloys during electrochemical post-processing

Picosecond laser drilling study of directional solidification Ni3Al-based superalloy

High-Cycle Fatigue Fracture Behavior and Stress Prediction of Ni-Based Single-Crystal Superalloy with Film Cooling Hole Drilled Using Femtosecond Laser

Experimental study of nickel-based superalloy IN792 with femtosecond laser drilling method

Microstructural Evolution and Formation of Fine Grains During Fatigue Crack Initiation Process of Laser Powder Bed Fusion Ni-based Superalloy

Hot corrosion mechanism of laser metal deposited Ni-based single crystal superalloy under fuel gas atmosphere

Effect of Laser Energy Density and Scanning Strategy on Residual Stress in Laser Melting Deposited FGH4096 Superalloy

Microstructural insights into fatigue short crack propagation resistance and rate fluctuation in a Ni-based superalloy manufactured by Laser powder bed fusion

An experimental investigation into the defects of laser-drilled holes in thermal barrier coated Inconel 718 superalloys

Investigating the Impact of Substrate Preheating on the Thermal Flow and Microstructure of Laser Cladding of Nickel-Based Superalloy

Research on Finite Element Simulation and Recrystallization of Laser Shock Peened Nickel-Based Single-Crystal Superalloy