Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Cyclic plasticity modeling and fatigue life assessment of the recasting material of a nickel-based superalloy induced by laser manufacturing

Microstructural characterization and fatigue performance of the recast material induced by laser manufacturing of a nickel-based superalloy

Shielding Effects on Fatigue and Crack Growth of the Recasting Zone Induced by Laser Manufacturing in a Nickel-Based Superalloy

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Multiscale Plasticity Behavior and Fatigue Performance of Laser Melting Multi-Layer Nickel-Based Superalloys Upon Heat Treatments

A Study of Fatigue Mesoscopic Elasto-Plastic Properties of a Nickel-Base Superalloy by Instrumented Microindentation Measurements

Investigation of fatigue mesoscopic mechanical properties of a nickel-based superalloy by instrumented microindentation measurements

Characterization of the Recasting-Affected Zone in the Nickel-Based Superalloy Upon Single-Pulse Laser Treatment

Stress Shielding in Laser Melting Multilayered Nickel-Base Superalloys under Monotonic and Cyclic Loadings

Effects of Recast Layer on Fatigue Performance of Laser-Drilled Holes in Nickel-Based Superalloy

Cyclic Plasticity Modeling of Nickel-Based Superalloy Inconel 718 under Multi-Axial Thermo-Mechanical Fatigue Loading Conditions

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Anisotropic Cyclic Plasticity Modeling for Additively Manufactured Nickel‐based Superalloys

Deformation Mechanisms of Selective Laser Melted 316l Austenitic Stainless Steel in High Temperature Low Cycle Fatigue

Multiscale analysis of interior cracking behavior of Ni-based superalloy fabricated by selective laser melting under very-high-cycle-fatigue at high-temperature

Effect of elevated temperature on high-cycle and very-high-cycle fatigue properties of Ni-based superalloy manufactured by selective laser melting

Quantitative Study of High-Frequency Fatigue Hole-Edge Stresses in Nickel-Based Single-Crystal Superalloy

Fatigue Life Assessment of a Porous Casting Nickel-Based Superalloy Based on Fracture Mechanics Methodology

Very-high-cycle fatigue behavior of AlSi10Mg manufactured by selected laser melting: Crystal plasticity modeling

Exploring the role of Type-II residual stresses in a laser powder bed fusion nickel-based superalloy using measurement and modeling

A modified damage-coupled viscoplastic constitutive model for capturing the asymmetric behavior of a nickel-based superalloy under wide creep-fatigue loadings