Effect of microstructure on the superelasticity of high-relative-density Ni-rich NiTi alloys fabricated by laser powder bed fusion

Jianbin Zhan,Jinzhou Wu,Ruijin Ma,Kun Li,Tingting Huang,Jinxin Lin,Lawrence E. Murr

DOI: https://doi.org/10.1016/j.jmatprotec.2023.117988

IF: 6.3

2023-04-19

Journal of Materials Processing Technology

Abstract:Superelastic Ni-rich NiTi alloy has received great attention in recent years due to its impressive shape-recovery capability without heating, especially possessing complex structures produced by laser powder bed fusion (LPBF). However, the trade-off between relative density, mechanical property, and superelasticity is difficult to balance. In this study, the microstructure and superelasticity of LPBFed NiTi alloys with different relative densities tuned by a self-developed operation window have been investigated comprehensively. The results show that increased scanning speed at high laser power leads to a lower volumetric energy density, resulting in a higher relative density of the alloy. NiTi alloys with high relative density (>99.5%) are successfully obtained at different laser powers based on this principle. The scattered micropores are present at low laser power, leading to crack propagation. In contrast, the high laser power produces a low-angle dislocation wall concentrated in the center of the melt pool, which is beneficial to the mechanical properties of the manufactured part. Moreover, the combination of high laser power and high scanning speed (HH) process is vital to improve the superelasticity of NiTi alloys with a relatively low M s than the original powder. It critically owes to the precipitates of Ti 4 Ni 2 O that enhance cyclic stability and recoverability. This paper provides a promising pathway for tuning the functional properties of NiTi alloys by the LPBF process to obtain a superelastic response balanced with mechanical properties.

materials science, multidisciplinary,engineering, manufacturing, industrial