Abstract:Advanced lightweight high-strength steels are often compositionally and microstructurally complex. While this complex feature enables the activation of multiple strengthening and strain-hardening mechanisms, it also leads to a complicated damage behavior, especially in the presence of hydrogen (H). The mechanisms of hydrogen embrittlement (HE) in these steels need to be properly understood for their successful application. Here we focus on a high-Mn (∼20 wt.%), high-Al (∼9 wt.%) lightweight steel with an austenite (∼74 vol.%) and ferrite (∼26 vol.%) two-phase microstructure and unravel the interplay of H-related decohesion and localized plasticity and their effects on failure. We find that HE in this alloy is driven by both, H-induced intergranular cracking along austenite-ferrite phase boundaries and H-induced transgranular cracking inside the ferrite. The former phenomenon is attributed to the mechanism of H-enhanced decohesion. For the latter damage behavior, systematic scanning electron microscopy-based characterization reveals that only parts of the transgranular cracks inside ferrite are straight (∼52% proportion) and along the cleavage plane. Other portions of these transgranular cracks show a distinct deviation from the {100} planes at certain stages of crack propagation, which is associated with a mechanism transition from the H-enhanced transgranular decohesion of the ferrite by cleavage to the H-associated localized plasticity occurring near the propagating crack tip. These mechanisms are further discussed based on a detailed comparison to the damage behavior at cryogenic temperatures and on the nanoindentation results performed with in-situ H-charging. The findings provide new insights into the understanding of the interplay between different HE mechanisms operating in high-strength alloys and their synergistic effects on damage evolution.

In-depth Understanding in the Effect of Hydrogen on Microstructural Evolution, Mechanical Properties and Fracture Micro-Mechanisms of Advanced High-Strength Steels Welded Joints

Interaction Between Dislocations, Precipitates and Hydrogen Atoms in a 2000 MPa Grade Hot-Stamped Steel

Effect of Plastic Strain Damage on the Hydrogen Embrittlement of a Dual-Phase (DP) and a Quenching and Partitioning (Q&P) Advanced High-Strength Steel

Embrittlement of Notched Duplex Stainless Steel: Role of Hydrogen-Assisted Void Growth and Cleavage

Experimental Investigation of the Effect of Hydrogen on Fracture Toughness of 2.25Cr-1Mo-0.25v Steel and Welds after Annealing

Hydrogen Embrittlement Behavior and Mechanism of Low Carbon Medium Manganese Steel Gas Metal Arc Welding Joints

Hydrogen embrittlement of high-strength marine steel as a weld joint in artificial seawater under cathodic polarization

Analysis of hydrogen-induced cracking mechanism in quenching and partitioning steels

Hydrogen embrittlement mechanisms in advanced high strength steel

Effect of hydrogen charging intensities and times on hydrogen embrittlement of Q&P980 steel

Hydrogen influence on some advanced high-strength steels

Effect of shearing prestrain on the hydrogen embrittlement of 1180 MPa grade martensitic advanced high-strength steel

Hydrogen Trapping Sites and Hydrogen-Induced Cracking in High Strength Quenching & Partitioning (Q&P) Treated Steel

Effect of fatigue damage on the hydrogen embrittlement sensitivity of X80 steel welded joints

Impact of hydrogen embrittlement on the tensile-shear property of resistance spot-welded advanced high-strength martensitic steels

Hydrogen Diffusion Mechanism of the Single-Pass Welded Joint in Welding Considering the Phase Transformation Effects

The hydrogen embrittlement mechanisms and hydrogen induced cracking process of selective laser-melted GH4169

Hydrogen-associated decohesion and localized plasticity in a high-Mn and high-Al two-phase lightweight steel

Formation Mechanism of Hydrogen-Induced Delayed Cracking in Weld Center of High-Strength Steel

Effect of microstructure on hydrogen embrittlement and hydrogen-induced cracking behaviour of a high-strength pipeline steel weldment

The Effect of Charging Conditions on Hydrogen Embrittlement Behavior of Ultra-High-strength Steel 22Mnb5