From Crack-Prone to Crack-Free: Eliminating Cracks in Additive Manufacturing of High-Strength Mg2Si-modified Al-Mg-Si Alloys

Tao Wen,Zhicheng Li,Jianying Wang,Yimou Luo,Feipeng Yang,Zhilin Liu,Dong Qiu,Hailin Yang,Shouxun Ji

DOI: https://doi.org/10.1016/j.jmst.2024.04.009

2025-01-01

Abstract:Large solidification ranges and coarse columnar grains in the additively manufacturing of Al -Mg -Si alloys are normally involved in hot cracks during solidification. In this work, we develop novel crack -free AlMg 2 Si alloys fabricated by laser powder-bed fusion (L-PBF). The results indicate that the eutectic Mg 2 Si phase possesses a strong ability to reduce crack susceptibility. It can enhance the grain growth restriction factor in the initial stage of solidification and promote eutectic filling in the terminal stage of solidification. The crack -free L-PBFed Alx Mg 2 Si alloys ( x = 6 wt.%, 9 wt.%, and 12 wt.%) exhibit the combination of low crack susceptibility index (CSI), superior ability for liquid filling, and grain refinement. Particularly, the L-PBFed Al-9Mg 2 Si alloy shows improved mechanical properties (e.g. yield strength of 397 MPa and elongation of 7.3 %). However, the cracks are more likely to occur in the region near the columnar grain boundaries of the L-PBFed Al-3Mg 2 Si alloy with a large solidification range and low eutectic content for liquid filling. Correspondingly, the L-PBFed Al-3Mg 2 Si alloy shows poor bearing capacity of mechanical properties. The precise tuning of Mg 2 Si eutectic content can offer an innovative strategy for eliminating cracks in additively manufactured Al -Mg -Si alloy. (c) 2024 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.