Abstract:The predominant method for improving the mechanical characteristics of aluminum -lithium (Al-Li) alloys during laser welding is by regulating the transition from columnar crystals to equiaxed crystals. The transition is facilitated through the incorporation of TiC particles, which play a crucial role in augmenting the strength and toughness of the aluminum alloy. The inclusion of TiC particles offers a new opportunity to enhance the utilization of Al-Li alloys in laser welding procedures. The main aim of this study is to control the transition from columnar to equiaxed crystal structures by creating a TiC nanoparticle-reinforced aluminum alloy filler wire. This is intended to improve the properties of laser -welded joints. The study investigates the impact of different TiC particle contents on the microstructural characteristics. The presence of TiC particles is noted to enhance the transformation of columnar crystals into equiaxed crystals in the welded joints, resulting in a refined microstructure. The augmentation of particle content results in a notable reduction in the average grain size, decreasing from 78.25 mu m to 37.15 mu m. This alteration shifts the directional growth preference from specific crystallographic axes to a stochastic trajectory. Significantly, when the particle content reaches 0.6 wt%, remarkable enhancements in both tensile strength and elongation are evident, resulting in an ultimate tensile strength of 318 MPa and an elongation of 4.8 %. The dispersed configuration of TiC particles plays a pivotal role in hindering the movement of dislocations, consequently increasing the energy necessary for this mechanism. Moreover, the existence of these particles at grain boundaries impedes the propagation of cracks by altering the direction of the crack path, absorbing additional energy, and consequently improving toughness. An evident pattern emerges when examining higher particle concentrations, indicating that a decrease in ultimate tensile strength is concomitant with an increase in elongation.

Coupling effects of SiC and TiB2 particles on crack inhibition in Al-Zn-Mg-Cu alloy produced by laser powder bed fusion

Microstructure evolution and mechanical properties strengthening in laser powder bed fusion of high-strength SiC and TiB 2 co-reinforced Al-Zn-Mg-Cu composites

Microstructure evolution and mechanical properties strengthening in laser powder bed fusion of high-strength SiC and TiB2 co-reinforced Al-Zn-Mg-Cu composites

Effective Control of Microstructure Evolution in AZ91D Magnesium Alloy by SiC Nanoparticles in Laser Powder-Bed Fusion

On the Si-induced microstructure evolution, solidification cracking healing and strengthening behavior of laser powder bed fusion additive manufactured Al-Cu-Mg/Si alloys

Cracking Behaviour and Its Suppression Mechanisms with TiB2 Additions in the Laser Additive Manufacturing of Solid-Solution-strengthened Ni-based Alloys

Controlling the Columnar-to-equiaxed Transition and Crack Propagation Behavior of Laser Welded Al-Li Alloy Reinforced with TiC Nanoparticles

Selective laser melting additive manufacturing of 7xxx series Al-Zn-Mg-Cu alloy: Cracking elimination by co-incorporation of Si and TiB2

Crack initiation mechanism of laser powder bed fusion additive manufactured Al-Zn-Mg-Cu alloy

Dual Beam Laser Fusion-Brazed Ti6Al4V/AA7075 Dissimilar Lap Joint: Crack Inhibition Via Inoculation with TiC Nanoparticles

Inhibition of Cracking by Grain Boundary Modification in a Non-Weldable Nickel-Based Superalloy Processed by Laser Powder Bed Fusion

Microstructure Evolution and Crack Prevention in TiC Nanoparticles-Enhanced 2195 Al Li Alloy Joint Fabricated by Coaxial Fiber-Diode Hybrid Laser Wire-Feeding Welding

Revealing the Precipitation Behavior of Crack-Free TiB2/Al-Zn-Mg-Cu Composites Manufactured by Laser Powder Bed Fusion

The role of ceramic particles on the crack inhibition and mechanical properties improvement of Haynes 230 alloy fabricated by laser powder bed fusion

Solidification Mechanism of Microstructure of Al-Si-Cu-Ni Alloy Manufactured by Laser Powder Bed Fusion and Mechanical Properties Effect

Liquid Phase Diffusion Bonding for SiC Particles Reinforced Aluminum Matrix Composites Using Pure Copper Inter-Layer

Laser additive manufacturing of Ti and Ce co-modified 2195 difficult-to-process aluminum alloy: Grain refinement, cracking suppression and enhanced mechanical properties

Laser powder bed fusion of crack-free 6061Al alloy using nano-sized TiO 2 modified powders

Reducing cracking sensitivity of CM247LC processed via laser powder bed fusion through composition modification

From Crack-Prone to Crack-Free: Unravelling the Roles of LaB6 in a Β-Solidifying TiAl Alloy Fabricated with Laser Additive Manufacturing

Design of a novel crack-free precipitation-strengthened nickel-based superalloy and composites for laser powder bed fusion