Revealing the Precipitation Behavior of Crack-Free TiB2/Al-Zn-Mg-Cu Composites Manufactured by Laser Powder Bed Fusion

Guichuan Li,Bensu Tunca,Seren Senol,Massimiliano Casata,Yi Wu,Zhe Chen,Kim Vanmeensel
DOI: https://doi.org/10.1016/j.addma.2023.103460
IF: 11
2023-01-01
Additive Manufacturing
Abstract:The microstructural evolution and precipitation behavior in additively manufactured age-hardenable TiB2/Al-Zn-Mg-Cu composites were investigated. As-built, direct-aged, solution-treated, and T6 heat-treated samples were characterized at macro, micro, and nano-scales to provide fundamental insights on the effect of the non-equilibrium L-PBF solidification microstructure and the presence of TiB2 reinforcement particles on the pre-cipitation behavior. Crack-free and near fully dense (99.7 %) TiB2/Al-Zn-Mg-Cu composites were successfully manufactured using L-PBF. The composites exhibited a fine equiaxed microstructure containing nanometer-and submicrometer-sized TiB2 particles, possessing an improved hardness compared to unreinforced Al-Zn-Mg-Cu alloys. The heterogeneous chemistry and the heterogeneously distributed dislocation density, both direct con-sequences of the rapid L-PBF solidification, were preserved in the direct-aged sample. The resulting non-uniform distribution of eta' precipitates led to a hardness of 200 +/- 5 HV, showing a 40 HV increase compared to the as-built sample. A solution heat treatment enabled the dissolution of interdendritic segregated elements in the as-built sample, resulting in a chemically homogeneous FCC-Al matrix. Simultaneously, it decreased the dislocation density and induced the formation of needle-shaped Al7Cu2Fe phases. The subsequent ageing treatment pro-moted a high density of well-dispersed eta' nanoprecipitates, leading to an overall Vickers hardness of 215 +/- 2 HV for the T6 sample. The TiB2/Al-Zn-Mg-Cu composite exhibited an accelerated precipitation behavior compared to the unmodified Al-Zn-Mg-Cu alloy, mainly due to heterogeneous precipitation on the TiB2 particles and the thermal expansion mismatch dislocations in the vicinity of the TiB2 particles, as well as enhanced diffusion along high-angle grain boundaries.
What problem does this paper attempt to address?