Abstract:Vat photopolymerization (VPP) 3D printing of ceramics normally uses ceramic slurries directly made of the target ceramic powder. It may become challenging when the ceramic powders are difficult-to-make and thus are expensive or rarely accessible. We have previously proposed a generative shaping and material-forming (GSM) 3D printing strategy, which involves the use of low-cost multi-component inorganic ceramic precursors as powder sources. The shaping of complex structures was realized through VPP, followed by reaction sintering to form the target ceramic material. In the current study, as a step further, ceramic (Li2CO3) and polymer (methyl polysiloxane) combined precursors were employed as an alternative material source for the first time to go through the 3D printing and reaction sintering processes, complementing the application range of the proposed GSM strategy. The slurry formulation and printability, the sinterability of the printed parts and the microstructures and mechanical performance of the sintered parts were characterized and optimized in accordance with the ingredient contents, particularly the stoichiometric ratios of Si:Li in the precursors. As a result, complex-structured Li4SiO4 ceramics with high purity were fabricated based on the use of Li2CO3 ceramic and Si-rich polymer as precursors. Through the advanced characterization and analysis of material phase and microstructural evolution, it was found that the fabricated complex-structured Li4SiO4 ceramics based on a precursor slurry with a solid content of 40 vol%, a Si:Li ratio of 1:2.5, and a sintering temperature of 850 °C showed a high phase purity of 97.23% and a compressive strength of 15.24 ± 0.33 MPa, with a skeleton’s relative density of 65.31% is achieved. The results showed greatly enhanced strength at much higher porosities, which might be advantageous and beneficial to structure engineering for mechanical enhancement and the improvement of tritium release effectiveness. Compared with the previous study using multi-component ceramic powder precursors, the ceramics prepared in this study exhibited enhanced microstructural stability and higher phase purity with an advantageously lower sintering temperature. Further analysis revealed that compared with the high temperature solid-state reaction of multi-component ceramic powder precursors, the involvement of the Si-rich polymer precursor enabled the more efficient and complete synthesis of Li4SiO4 as a result of the accelerated covering and cleavage of Si–O–Si bonds on the Li2CO3 particles at a much lower temperature. The present work suggests that the GSM strategy using combined ceramic and polymer precursors as proposed in this study is a promising alternative method to produce high quality Li4SiO4 components with complex structures.

Preparation and Properties of Si3N4 Ceramics Via Vat Photopolymerization Using Si3N4 Powders Coated with Bowl-Like Boehmite

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Preparation and properties of Si3N4 ceramics via digital light processing using Si3N4 powder coated with Al2O3-Y2O3 sintering additives

Preparation of high‐strength Si3N4 ceramics via vat photopolymerization: A bi‐phase particle size gradation strategy

Investigation of curing behavior and mechanical properties of SiC ceramics prepared by vat photopolymerization combined with pressureless liquid-phase sintering using Al 2 O 3 -coated SiC powder

Preparation of porous Si 3 N 4 ceramics via tailoring solid loading of Si 3 N 4 slurry and Si 3 N 4 poly-hollow microsphere content

Effects of Ceramic Powder Coating Treatment on the Curing Behavior, Mechanical Properties, and Microstructure of 3D Printed Silicon Nitride Ceramics

Si 3 N 4 slurry with high solid phase, low viscosity prepared via surface-oxidation and silane coupling agent modification hybrid method

3D Printing and in Situ Transformation of SiCnw/SiC Structures

Influence of the Dispersants and Sintering Process on the Properties of Si2N2O Ceramics Via Digital Light Processing

Optimizing AlN hydrolysis process to fabricate coated modified powders for improving the properties of Si 3 N 4 /SiAlON ceramics prepared by Vat Photopolymerization

Fabrication and properties of Si2N2O-Si3N4 ceramics via direct ink writing and low-temperature sintering

Influence of the content of polymethyl methacrylate on the properties of porous Si3N4 ceramics fabricated by digital light processing

Preparation of porous Al2O3 ceramics with enhanced properties by SLS using Al2O3 poly-hollow microspheres (PHMs) coated with CaSiO3 sintering additive

Si3N4 Hollow Microsphere Toughened Porous Ceramics from Direct Coagulation Method Via Dispersant Reaction

3D printing Si3N4-bonded SiC refractories fabricated using colloidal films-containing slurries based on non-spherical SiC and Si powders

Novel porous Si3N4 ceramics prepared by aqueous gelcasting using Si3N4 poly-hollow microspheres as pore-forming agent

Preparation And Properties Of High Strength Porous Si3n4 Ceramics

Mechanical and dielectric properties of Si3N4/β-SiAlON composite ceramics fabricated by vat photopolymerization 3D printing technology

Fabrication of broadband wave-transparent Si 3 N 4 ceramics with octet-truss lattice structure by vat photopolymerization 3D printing technology

Generative shaping and material-forming (GSM) enables structure engineering of complex-shaped Li4SiO4 ceramics based on 3D printing of ceramic/polymer precursors