Abstract:Ti(C,N)-xCrMnFeCoNi-(15wt.%-x)Ni cermets (x = 0wt.%, 5wt.%, 10wt.%, 15wt.%) were fabricated by low-pressure sintering. Because of the sluggish diffusion effect of high-entropy alloy (HEA), the grain growth of cermets containing HEA binder is inhibited. The FCC binder phases of cermets with CrMnFeCoNi/Ni binders generate a uniform dispersion, motivating to form many complete and moderate rim phases and wet the ceramic particles. Furthermore, the hardness of cermets roughly increases, while the strength and fracture toughness maintain the change tendency of rising the peak and then falling with CrMnFeCoNi additions. Ti(C,N)-5wt.% CrMnFeCoNi-10wt.% Ni cermets obtains a prominent mechanical property combination with hardness of 1646 ± 13.5 HV30, strength of 2181 ± 167.2 MPa and fracture toughness of 9.1 ± 0.11 MPa m1/2. Besides, the cermets containing CrMnFeCoNi/Ni binders obtain reduced friction coefficients and low wear rates at 750 °C compared with Ti(C,N)–Ni cermets and Ti(C,N)-HEA cermets. The superior high-temperature wear resistance is ascribed to the thermal softening resistance of CrMnFeCoNi, strengthening and toughening effect of CrMnFeCoNi/Ni on matrix and the transition of wear mechanism from abrasive wear and the removal of tribochemical layers to the removal of tribochemical layers. The cutting lifetime of cermets containing CrMnFeCoNi/Ni binders is increased by 40%–70% in comparison with Ti(C,N)–Ni cermets during machining 17-4 PH stainless steel. Concisely, Ti(C,N)-based cermets with outstanding mechanical, wear resistance and cutting properties can be obtained by partially replacing Ni with 5–10 wt.% CrMnFeCoNi.

Insights into Hardening and Strengthening in Ultrafine Ti(C, N)-Based Cermets

Enhanced Densification of Ultrafine Ti(C, N)-based Cermets Based on Grain-Growth Induced Liquid-Phase Pore Filling Mechanism

Tuning microstructure for superb mechanical properties in a Ti(C,N)-(WMoTaNbTi)C-Ni/Co cermets via change sintering temperature

Achieving hardness‐strength‐toughness synergy in (Ti, W, Mo, Cr)(C, N)‐based cermets

Strengthening and toughening of Ti(C,N)-based cermets: (Ti,W)C additive design and the mechanism

Cutting Performance and Wear Mechanism of Submicron and Ultrafine Ti(C, N)-based Cermets

Submicron Ti(C,N)-based cermets with improved microstructure using high-energy milled and subsequent heat-treated ultrafine Ti(C,N) powders

Microstructure, Interface Characteristics and Mechanical Properties of Ti(C,N)-based Cermets with a Cellular Structure

Correlation between microstructure and mechanical properties of Ti(C,N)-xWC-Ni cermets prepared by mechanical activation and subsequent in situ carbothermal reduction

Influence of TaC content on microstructure and mechanical performance of Ti(C,N)-based cermets fabricated by mechanical activation and subsequent in situ carbothermal reduction

Improvement of microstructure, mechanical properties and cutting performance of Ti(C,N)-based cermets by ultrafine La2O3 additions

Properties of Ti(C,N)-based cermets reinforced with ZrO2 whiskers deposited via sulfate flux at high temperatures

Fabrication, microstructure evolution, and mechanical properties of Ti(C,N)-HfN-WC-Ni-Mo cermets

Effects of CrMnFeCoNi additions on microstructure, mechanical properties and wear resistance of Ti(C,N)-based cermets

Preparation of Ultra-Fine ATC Ceramics and Analysis of Its Dry-Sliding Wear Behavior

Effect of Cr2C3 addition on microstructure and mechanical properties of Ti(CN)-based cermets

Development of TiCN-based cermets: Mechanical properties and wear mechanism

Effect of Si3N4 Additive on Microstructure and Mechanical Properties of Ti(C,N)-Based Cermet Cutting Tools

Effect of ZrO2 Whiskers on the Microstructure and Mechanical Properties of a Ti(C,N)‐based Cermet Cutting Tool Material

Effect of Cr<sub>2</sub>C<sub>3</sub> Addition on Microstructure and Mechanical Properties of Ti(CN)-Based Cermets

Effects of the addition of multi-walled carbon nanotubes on the microstructure and properties of Ti(C,N)-based cermets prepared by spark plasma sintering