Abstract:Electrical characterization of semiconducting oxide nanowires (NWs) is mostly performed using complex techniques, which necessitates a series of costly nanofabrication procedures. In this work, with the aim to provide a low-cost, feasible, facile, and reproducible approach for enabling the study of NW electrical properties, we report direct electrical measurements on individual and overlapped suspended zinc oxide NWs (ZnO NWs). We have succeeded in constructing both two- and three-terminal devices simply by employing tungsten (W) nanoprobes with the aid of a nanomanipulation system embedded inside a scanning electron microscope’s vacuum chamber. Stable contacts were established using the Joule heating effect and e-beam exposure at the junctions between the NW and the pre-cleaned W tips. P-channel field-effect transistor devices were achieved with an on–off current ratio of ∼101, a threshold voltage (>1.5 V), a transconductance of ∼16 μS, a sub-threshold swing of ∼220 mV/decade, and field-effect carrier mobility roughly estimated to be around 926.4 cm2/(V·s) after correction for contact resistances/optimization. The average resistivity of ZnO NWs was calculated to be ∼2.23 × 10–2 Ω·cm for NWs with diameters between 70 and 500 nm. Besides, we have demonstrated a contact resistance of ∼19.60 kΩ and a Schottky barrier height of ∼0.37 eV present at W/ZnO NW interfaces. The contact resistance between two overlapped ZnO NWs was estimated to be ∼283 kΩ, which is relatively higher than that offered between W/ZnO NWs. This work provides a solid experimental procedure to address true intrinsic electrical properties at metal/semiconductor interfaces, and our findings have potential applications in next-generation 3D suspended ZnO NW-based nanoelectronic devices.

Study on the Structural and Physical Properties of ZnO Nanowire Arrays Grown Via Electrochemical and Hydrothermal Depositions

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Effects of Electrodeposition Electrolyte Concentration on Microstructure, Optical Properties and Wettability of ZnO Nanorods

Effect of Electrodeposition Time on Microstructure, Wettability and Optical Properties of ZnO Nanorod Arrays

ZnO Nanowire and $\hbox{ws}_{2}$ Nanotube Electronics

Study on the microstructure and growth mechanism of electrochemical deposited ZnO nanowires

Growth And Characterization Of Cu-Catalyzed Zno Nanowires

Arrays of ZnO Nanowires Fabricated by a Simple Chemical Solution Route

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

Temperature dependant structural and electrical properties of ZnO nanowire networks

Effect of Growth Time and Annealing on the Structural Defect Concentration of Hydrothermally Grown Zno Nanowires

Facile and Controllable Growth of ZnO 1D Nanostructure Arrays on Zn Substrate by Hydrothermal Process

Optical and Electrical Properties of Ga-Doped ZnO Nanowire Arrays on Conducting Substrates

Synthesis and Electrical Properties of ZnO Nanowires

Optical and Electrical Performance Of, Sno2 Capped Zno Nanowire Arrays

Characterization of Electrical Properties of Suspended ZnO Nanowires Using a Nanorobotic Manipulation System Inside a Scanning Electron Microscope for Nanoelectronic Applications

Synthesis and electrical properties of ZnO nanowires.

ZnO@Co Hybrid Nanotube Arrays Growth from Electrochemical Deposition: Structural, Optical, Photocatalytic and Magnetic Properties

Large-Scale Synthesis of Bicrystalline ZnO Nanowire Arrays by Thermal Oxidation of Zinc Film: Growth Mechanism and High-Performance Field Emission

Improved seedless hydrothermal synthesis of dense and ultralong ZnO nanowires.

Controllable growth and optical properties of ZnO nanostructures on Si nanowire arrays