Abstract:Magnesia-chrome refractories have been essential materials for application as wear lining in copper production furnaces for many years. Formation of hexavalent chromium (Cr(VI)) has been a major concern despite its admirable corrosion resistance in copper slag. Magnesia-chrome refractory specimens (9, 12, 15 and 18 wt% Cr2O3) with addition of Al2O3 and TiO2 were fabricated and subsequent corrosion tests using copper slag was conducted in air. The corrosion mechanism between magnesia-chrome refractories fabricated and synthetic copper slag were investigated by means of X-ray diffraction (XRD) and scanning electron microscope (SEM), and concurrent formations of Cr(VI) were assessed effectively by leaching test. All the magnesia-chrome specimens prepared are composed of periclase and composite spinel Mg(Al,Cr,Ti)(2)O-4 phases after firing at 1700 degrees C. Densification of the specimens decreases with the increase in Cr2O3 content due to the increased volume expansion, while TiO2 addition can improve their densification as mass transfer is enhanced during the sintering process. The corrosion resistance of the specimens decreases slightly with the Cr2O3 content due to the increased apparent porosity, which would result in penetration of more corrosive slag at the initial stage of the corrosion test while a newly formed (Mg,Cu)(Cr,Fe)(2)O-4 spinel dense layer between the slag and penetration layer effectively hinders further penetration of slag and well protects the specimens. The Cr(VI) in the specimens prepared increases obviously with the Cr2O3 added content, while the TiO2 addition can suppress the formation of Cr(VI) effectively and the copper slag can cause the formed Cr(VI) to be reduced further during the corrosion process. For all the specimens, concentrations of Cr(VI) in the leachates is much lower than the US-EPA limit of 100 mg/kg but exceeds the European limit of 2 mg/kg after the corrosion test. (C) 2019 Elsevier B.V. All rights reserved.

Chromium: A Double-Edged Sword in Preparation of Refractory Materials from Ferronickel Slag

Chromium-promoted preparation of forsterite refractory materials from ferronickel slag by microwave sintering

Facile Route for Preparing Refractory Materials from Ferronickel Slag with Addition of Magnesia

Preparation of Refractory Materials by Co-sintering of Ferronickel Slag and Ferrochromium Slag: Thermodynamic Analysis

Preparation of Refractory Materials from Ferronickel Slag

From ferronickel slag to value-added refractory materials: A microwave sintering strategy

Preparation of Refractory Materials from Electric Furnace Ferronickel Slag and Blast Furnace Ferronickel Slag: A Comparison

Promoting Spinel Formation and Growth for Preparation of Refractory Materials from Ferronickel Slag

Assessing Magnesia Effect on Preparing Refractory Materials from Ferrochromium Slag

Alumina-enhanced Valorization of Ferronickel Slag into Refractory Materials under Microwave Irradiation

Thermodynamic Characteristics of Ferronickel Slag Sintered in the Presence of Magnesia

Valorization of Ferronickel Slag into Refractory Materials: Effect of Sintering Temperature

Enhanced Chromium Recovery in the Smelting of Ferronickel Along with Energy-Saving: An Industrial Case Study

Synergistic preparation of forsterite‐spinel refractory materials from ferronickel slag and ferrochromium slag

Corrosion Mechanism of Magnesia-Chrome and Alumina-Chrome Refractories in E-scrap Smelting

Corrosion Mechanisms of Magnesia-Chrome Refractories in Copper Slag and Concurrent Formation of Hexavalent Chromium

Behavior of chromium in the reduction and smelting of high alumina nickel laterite in blast furnace

Effect of Phase Composition on Leaching Behavior and Mechanical Properties of Ceramics from Ferrochrome Slag and Tundish Slag

Enhancement, application, and challenges of chromium–corundum high‐temperature refractories

Enhanced Mechanical Properties and Thermal Shock Resistance of Magnesia Refractories Via in Situ Formation of Tetragonal Zirconia

Effects of Sintering Temperature and Time on Preparation of Refractory Materials from Ferronickel Slag Under Microwave Irradiation