Abstract:Because of the low utilization rate, a large amount of metallurgical slag was piled up or buried each year, resulting in serious environmental pollution and resource waste. This study focused on the value-add utilization of secondary aluminum dross (SAD) and ferronickel slag (FNS) by preparing porous cordierite-mullite ceramics (CMC) for thermal insulation. The detailed thermodynamic calculation of the preparing process was carried out by using the phase diagram and equilibrium component function module in FactSage 8.1 software, which provided precise theoretical guidance for the practical synthesis experiment. The phase component, microstructure, and mechanical and thermal insulation properties of the prepared CMC at an FNS addition from 5 to 30 wt% were investigated by an X-ray diffractometer, scanning electron microscopy assembled with an energy-dispersive spectrometer, and a laser thermal conductivity testing instrument, respectively. It was shown that the original mineral phase of the raw materials applied can be converted to cordierite, mullite, and spinel after sintering at 1350 degrees C, which results in higher strength and lower thermal conductivity of the prepared ceramics. Moreover, the increase of FNS addition promoted the content of cordierite and the microstructure densification of CMC. With the increase of FNS addition, the apparent porosity of CMC decreased from 41.7% to 34.4%, and the average pore size varied from 46.7 to 29.0 mu m. The CMC with the lowest thermal conductivity of 0.86 W/(m K) was achieved at 20 wt% of FNS addition, which also had a good compressive strength of 52.8 MPa. The results proved the feasibility of preparing high-strength thermal insulation ceramics by recycling hazardous metallurgical slag of SAD and FNS, proposing a novel route for high value-added utilization of industrial solid waste.

Preparation of Refractory Materials by Co-sintering of Ferronickel Slag and Ferrochromium Slag: Thermodynamic Analysis

Preparation of Refractory Materials from Ferronickel Slag

Facile Route for Preparing Refractory Materials from Ferronickel Slag with Addition of Magnesia

Thermodynamic Characteristics of Ferronickel Slag Sintered in the Presence of Magnesia

Preparation of Refractory Materials from Electric Furnace Ferronickel Slag and Blast Furnace Ferronickel Slag: A Comparison

Valorization of Ferronickel Slag into Refractory Materials: Effect of Sintering Temperature

Synergistic preparation of forsterite‐spinel refractory materials from ferronickel slag and ferrochromium slag

Promoting Spinel Formation and Growth for Preparation of Refractory Materials from Ferronickel Slag

Chromium: A Double-Edged Sword in Preparation of Refractory Materials from Ferronickel Slag

Assessing Magnesia Effect on Preparing Refractory Materials from Ferrochromium Slag

Chromium-promoted preparation of forsterite refractory materials from ferronickel slag by microwave sintering

From ferronickel slag to value-added refractory materials: A microwave sintering strategy

Alumina-enhanced Valorization of Ferronickel Slag into Refractory Materials under Microwave Irradiation

Development of Refractory Material from Water Quenched Granulated Ferrochromium Slag

Effects of Sintering Temperature and Time on Preparation of Refractory Materials from Ferronickel Slag Under Microwave Irradiation

Preparation of Ferronickel from Nickel Laterite Via Coal-Based Reduction Followed by Magnetic Separation

Strengthening Sintering Of Limonitic Nickel Laterite By Substituting Ferronickel Tailings For Sintering Fluxes

Co-utilization of ferronickel slag and fly ash cenosphere for production of superior thermal insulation materials

Tailoring Tactics for Preparation of Superior Thermal Insulation Materials from Blast Furnace Ferronickel Slag: Control of Sintering Temperature

From Waste to Wealth: Converting Ferronickel Slag to MgO–Al2O3–SiO2 Castables

Co‐utilization of Secondary Aluminum Dross and Ferronickel Slag for Preparation of Cordierite–mullite Insulating Ceramic