Abstract:This study aims to prepare novel precursor powders for 8 mol% yttria-stabilized zirconia nano-powders. Precursor powders were extracted from the ethanol-water solution, which utilizes the changing solvation energy for different ions impacted by ethanol. An aqueous solution containing zirconium sulfate tetrahydrate and yttrium sulfate octahydrate was mixed with different volumes of ethanol to prepare precursor powders, then calcinating to obtain 8 mol% yttria-stabilized zirconia nano-powders. The scanning electron microscope and particle size measurements for precursor powders suggested that the ideal volume ratio between ethanol and the aqueous solution was 2.5, corresponding to the complete precipitation and well-dispersion. The X-ray diffraction measurements, crystallization kinetics calculations, and scanning electron microscope after calcinating precursor powders indicated the successful formation of 8 mol% yttria-stabilized zirconia powders and the particle growth through a one-dimensional growth mechanism in the 60-120 nm size range. The densification experiments and electrochemical performance measurements after sintering 8YSZ nano-powders showed high density and high ionic conductivity compared with commercial powders. An efficient process, successfully designed to achieve the commercial requirement, was used to prepare 8YSZ nano-powders.

On the Preparation of High-Surface-Area Nano-Zirconia by Reflux-Digestion of Hydrous Zirconia Gel in Basic Solution

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Preparation of Zirconia Powders by Sol-gel Process

Erratum to “Catalysis of dispersed silver particles on directional etching of silicon” [Appl. Surf. Sci. 254(10) (2008) 3061–3066]

Internal Nano Voids in Yttria-Stabilised Zirconia (YSZ) Powder

Preparation of High Surface Area Zirconia by RefluxDigestion in Basic Solutions

Hydrothermal Synthesis and Characterization of Zirconia Nanocrystallites

Design and Size Control of Uniform Zeolite Nanocrystals Synthesized in Adjustable Confined Voids Formed by Recyclable Monodisperse Polymer Spheres

Correction: Liu, Y.; Yang, J. Hydrophobic Modification of ZrO2-SiO2 Xerogel and Its Adsorption Properties to Rhodamine B. Gels 2022, 8, 675

From modification to mechanism: Supercritical hydrothermal synthesis of nano-zirconia

Study on a new, environmentally benign method and its feasibility of preparing nanometer zirconia powder

A Novel Route for the Preparation of Ultrafine Yttria-Doped Zirconia Powders

Correction: An ultrasound-induced MXene doped PAM–SA super-tough hydrogel

Preparation and Performance for Zirconia/Alumina Composite Ceramics

Correction: Fabrication of Asymmetrical Diffusion Dialysis Membranes for Rapid Acid Recovery with High Purity

Ethanol-induced formation of precursor for 8mol% Yttria-stabilized zirconia: Towards the production of well-dispersed, easily sintering, and high-conductivity nano-powders

Heat Treatment During Preparation of Nano-zirconia Powders by the Liquid-phase Process

Effects of Precipitators and Surfactants on the Preparation of Zirconia Nanopowders via Solvothermal Method

Solvothermal Synthesis of Zirconia Nanomaterials: Latest Developments and Future

Zirconia nano-colloids transfer from continuous hydrothermal synthesis to inkjet printing

Preparation of Zirconia Base Solid Solution Nanopowder by Exothermal Solid-State Synthesis