The Chemical Stability and Conductivity of BaCe0.9−xYxNb0.1O3−σ Proton-Conductive Electrolyte for SOFC
Kui Xie,Ruiqiang Yan,Xiaoxiang Xu,Xingqin Liu,Guangyao Meng
DOI: https://doi.org/10.1016/j.materresbull.2009.02.015
IF: 5.6
2009-01-01
Materials Research Bulletin
Abstract:BaCe0.8Y0.2O3−δ and BaCe0.9−xYxNb0.1O3−δ (x=0.1, 0.15, 0.2, 0.25, 0.3, 0.35) were prepared by a solid-state reactions. It was found that the BaCe0.8Y0.2O3−δ samples decomposed into CeO2 and BaCO3 after being exposed in the atmosphere (3% CO2+3% H2O+94% N2) at 700°C for 10h. However, samples containing Nb remains unchanged in the same conditions, demonstrating a better stability in the presence of CO2 and H2O. The conductivity of BaCe0.9−xYxNb0.1O3−δ increased with the increase of Y content (x≤0.30), and the highest value was observed at x=0.30 where a significant decrease in conductivity took place at x=0.35. The conductivity of BaCe0.6Y0.3Nb0.1O3−δ reaches 0.01S/cm in humid hydrogen at 700°C, slight lower than BaCe0.8Y0.2O3−δ, 0.012S/cm in the same conditions. Fuel cell with BaCe0.6Y0.3Nb0.1O3−δ as-prepared was successfully prepared and humidified hydrogen was supplied as fuels in evaluating the fuel cell performance. The open circuit voltage, peak power density and interfacial resistance at 700°C were 1.02V, 345mW/cm2 and 0.27Ωcm2, respectively.