Sintering of Zirconium Diboride Through Fe-based Liquid Phase

Sang‐Kuk Woo,In-Sub Han,H S Kim,Jianfeng Yang,E S Kang,C H Kim
1996-01-01
Abstract:In the present study, the effect of the addition of Fe on the pressureless and hot press sintering behavior was studied under Ar atmosphere. Pressureless sintering was performed 1900{approx}2000{sup o} C under Ar atmosphere. The addition of 1 wt.% Fe was increased effectively of the sintered density. However it was impossible to obtain high density higher than 90%. Zr-Fe-B compound in liquid phase was observed from the EDS and WDS analysis. It was considered that sinterability was enhanced due to the mass transfer through Fe based liquid phase formed at the sintering temperature. Hot pressing was performed at 1600{approx}1700{sup o} C under Ar atmosphere for 1 hr. It was possible obtain 95% relative density of ZrB{sub 2} specimen which is higher density at pressureless sintering. It could be thought that ZrB{sub 2} particles was rearranged through liquid phase by applied pressure during initial stage of sintering. 14 refs., 2 tabs., 12 figs.
What problem does this paper attempt to address?