Abstract:By employing an in-situ reaction pressureless sintering method, self-reinforced and SiC-B4C-ZrB2 multiphase composites were successfully prepared. The effect of TiO2 and ZrO2 additions on the sintered density, microstructure, and mechanical properties of the composites was investigated. TiO2 and ZrO2 were completely transformed into TiB2 and ZrB2 phases during the sintering process, and their appropriate addition helped enhance the relative density of the composites. In the SiC-B4C-TiB2 (SBT) composite, the introduction of TiB2 facilitated grain growth in all phases. The composite with 12 vol% TiB2 (SBT12) exhibited optimal mechanical properties, with Vickers hardness, fracture toughness, and flexural strength reaching 30.1±0.8 GPa, 5.17±0.23 MPa·m1/2, and 491±24 MPa, respectively. In the SiC-B4C-ZrB2 (SBZ) composite, the presence of ZrB2 resulted in the formation of a ternary eutectic liquid phase, SiC-B4C-ZrB2, during the sintering process, leading to grain coarsening and the generation of plate-like SiC grains. Among them, the composite with 6 vol% ZrB2 (SBZ6) demonstrated the best overall performance, with Vickers hardness, fracture toughness, and flexural strength of 29.7±0.6 GPa, 6.17±0.36 MPa·m1/2, and 443±22 MPa, respectively. Additionally, SBZ9 exhibited the highest fracture toughness, reaching 6.43±0.44 MPa·m1/2, with the pull-out of plate-like grains considered as the primary contributing factor. This study provides a reference for the preparation of high-strength and tough SiC-B4C-MeB2 multiphase composites through low-temperature pressureless sintering.

Pressureless Sintering of Zrb2-Sic Composites Strengthening by Ultra-Fine Ceramic Powders

Pressureless Sintering of ZrB2-SiC Ceramics Incorporating Sol-Gel Synthesized Ultra-Fine Ceramic Powders

Pressureless Sintering of High‐Density ZrB2–SiC Ceramic Composites

In Situ Synthesis of Ultrafine Zrb2-Sic Composite Powders and the Pressureless Sintering Behaviors

The Effect of Tio2 and Zro2 Additives on the Density, Microstructure, and Mechanical Properties of Pressureless Sintered Sic-B4c

Properties of ZrB2-SiC Ceramics by Pressureless Sintering

Pressureless Sintering of Silicon Carbide Ceramics Containing Zirconium Diboride

In Situ Synthesis Mechanism and Characterization of ZrB2–ZrC–SiC Ultra High-Temperature Ceramics

Microstructure and Mechanical Properties of ZrB2-SiC Composites

The impact of Si3N4 incorporation on the mechanical characteristics of ZrB2-SiC nanocomposite sintered via pressureless method

Microstructure and mechanical properties of pressure‐less sintered B4C–SiC–ZrB2–LaB6 ceramic composites

Pressureless Sintering of ZrC-based Ceramics by Enhancing Powder Sinterability

Preparation and Properties of B4c-Zrb2-Sic Ceramic Composites

Preparation and Mechanical Properties of ZrB2-based Ceramics Using MoSi2 As Sintering Aids

Processing and Mechanical Properties of Zirconium Diboride‐Based Ceramics Prepared by Spark Plasma Sintering

Pressureless Sintering of ZrB2–SiC Ceramics: the Effect of B4C Content

Oxidation Behaviors of the Pressureless Sintered ZrB<SUB>2</SUB>-SiC Composites: Oxidation Behaviors of the Pressureless Sintered ZrB<SUB>2</SUB>-SiC Composites

Densification, microstructure and mechanical properties of ZrB2–SiCw ceramic composites

Spark plasma sintering of B4C–ZrB2 and B4C–ZrB2–SiC ceramics

Effects of SiC Platelet and ZrSi2 Additive on Sintering and Mechanical Properties of ZrB2-based Ceramics by Hot-Pressing

Low-Temperature Sintering Behavior and Mechanical Properties of Bn-Zro2-Sic Composites