Preparation and Characterization of Cr-free passivation films on zinc coating using Response Surface Methodology and Electrochemical Methods
Yuhan Yao,Zhaolin Zhan,Jianxiong Liu,Xiao Wang,Xiaohua Yu,Ju Rong,
DOI: https://doi.org/10.20964/2019.09.07
IF: 1.541
2019-09-01
International Journal of Electrochemical Science
Abstract:Response surface methodology (RSM) was used in this study to determine the optimum operating conditions for the reduction of galvanized sheet corrosion using a Cr-free passivation films. Passivation films layer with strong corrosion resistance was formed on the surface of galvanizing which was impregnated in chromium-free passivating agent. Furthermore, the RSM was used to ascertain the main and interactive effects (deviation between the experimental and theoretical values: 0.12%). The coefficient of determination (R2) showed that the RSM approach was appropriate for optimization of the Cr-free passivator. Silane coupling agent, ammonium molybdate, nanosilica, and tannic acid played a key role in changing the corrosion area and potential. The results revealed that, compared with Cr6+ passivation, Cr-free passivation yielded considerably more homogeneous and smoother surfaces (surface roughness of Cr-free passivation film: 0.54 μm). In addition, the properties of the zinc coating after Cr- free passivation were clearly superior to those of the zinc coating subjected to the conventional Cr6+ passivation treatment. Ecorr, current density, and polarization resistance values of this superior coating were -1073 mV, 0.017 A cm-2, and 989.2 Q, respectively. This study can serve as an experimental and a theoretical guide for the development of Cr-free passivation films.
electrochemistry