Abstract:A Zn-Sn coating of ~30 μm thickness was prepared on an iron substrate by mechanical deposition using zinc and tin powders as raw materials. The Zn-Sn coating consists of zinc powder particles physically stacked with tin powder particles and filled with reduced tin, and the tin content in the coating is 20%–30%. The resulting Zn-Sn coating was characterized and analyzed with scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), polarization curves (Tafel), electrochemical impedance (EIS), and energy dispersive X-ray spectrometry (EDS). The results showed that the Zn powder was co-deposited with the Sn powder in a portable manner and the Sn powder was deflected and deformed to a great extent. The spot-flocculated reduced Sn also covered the surface of the Zn powder to fill the interstices of the coating to make the coating more compact. Compared with the pure Zn coating, the Zn-Sn coating has a positive shift of 68 mV in the self-corrosion potential in the polarization test, and the corrosion current was only 20% of that of the pure Zn coating. The reduced Sn had a shielding effect on the Zn powder and at the same time, in combination with inert tin powder, the polarization resistance of the plated layer increased to 1118 Ω/cm2. Furthermore, compared to the pure zinc layer, the time of white rust and red rust increased by 24 and 240 h, respectively. In addition, the XPS results showed that the Zn-Sn plating layer was clearly passivated, which was mainly due to the formation of Zn(OH)2 and Sn(OH)2. The results also emphasized that the tin element in the Zn-Sn plated layer can maintain the morphology of zinc powder, compact the plating layer, and prevent the release of corrosion products, thus improving the corrosion resistance of the Zn-Sn coating.

Formation Mechanism of Passivation Film on Tin-Plated Steel Sheet

Design of a Ti-Zr-P-Si Chromium-Free Passivation Composite Film with High Corrosion Resistance and Eco-Friendliness on Tinplate

Passivation and Chemical Conversion Combined Multi-Elements Coating on Low Sn-Coated Steel for Corrosion Protection

Trivalent chromium passivation for zinc coating and sealing of passivation film

Passivation and Depassivation of HPB335 Carbon Steel in Simulated Concrete Pore Solution

An Electrochemical Study on the Corrosion Behavior of the Tin Plate with Metal Drink Cans

Electrochemical Nucleation and Growth of Sn Onto Double Reduction Steel Substrate from a Stannous Fluoborate Acid Bath

Effect of Tin on the Corrosion Resistance of 16 Cr Ferritic Stainless Steel in Acidic Solution and Chloride-Containing Media

Investigations on corrosion resistance of steel coated with chromium-free ZTM conversion coating

Study on environment-friendly passivation for hot-dip galvanized steel with high corrosion resistance

Characterization of Al-induced electroless tin films on mild steel substrate for corrosion protection

Study on Microstructure and Properties of Mechanically Deposited Zn-Sn Coating

Preparation and Characterization of Cr-free passivation films on zinc coating using Response Surface Methodology and Electrochemical Methods

Atomistic Insights into the Deposition of Corrosion Products on the Surfaces of Steels and Passivation Films

Effects of Silanes on the Structure and Properties of Chromium-Free Passivation

Local Fine Structural Insight into Mechanism of Electrochemical Passivation of Titanium.

Preparation and performance study of manganate and PU composite passivation film

Passivation and depassivation properties of Cr–Mo alloyed corrosion-resistant steel in simulated concrete pore solution

Inhibition of Surface Corrosion Behavior of Zinc-Iron Alloy by Silicate Passivation

Inhibition Effect and Mechanism of Tin on the Active Dissolution of Tin-Containing 430LX Ferritic Stainless Steel

Composition and Structure of the Passive Film of 304 Stainless Steel in an Occluded Solution