Inhibition of Surface Corrosion Behavior of Zinc-Iron Alloy by Silicate Passivation

Fan Cao,Peng Cao,Yangyang Li,Yi Wang,Lei Shi,Di Wu
DOI: https://doi.org/10.3390/coatings13061057
IF: 3.236
2023-06-07
Coatings
Abstract:The passivation of zinc alloy coating was achieved through the utilization of both silicate and trivalent chromium passivation systems, employing a specific process formula consisting of Co(NO3)2 at a concentration of 2.5 g/L, C76H52O46 at 3 mL/L, Na2SiO3 at 25 g/L, C6H5Na3O7 at 15 g/L, and an appropriate amount of organic accelerator. The composite passivation of silicate and tannic acid was found to be more effective than the trivalent chromium passivation film, as it successfully eliminated the dendrite structure on the coating surface and reduced surface defects. The coordination between negatively charged SiO2− or SiO2 micelles and Zn2+ results in the formation of a passivation film that exhibits lower corrosion current and higher corrosion potential compared to the trivalent chromium passivation film. Additionally, the impedance test fitting results indicate that the silicate passivation film possesses a higher resistance value. Overall, the proposed silicate passivation system presents a viable alternative to the toxic chromate passivation system, offering non-toxicity and superior protective performance relative to the trivalent chromium passivation system.
materials science, multidisciplinary,physics, applied, coatings & films
What problem does this paper attempt to address?
### Problems the Paper Attempts to Solve This paper primarily investigates methods to inhibit the corrosion behavior on the surface of zinc-iron alloy through silicate passivation technology. Specifically, the paper explores the effectiveness of passivating zinc alloy coatings using silicate and trivalent chromium passivation systems, and compares the effects of these two methods. #### Main Issues: 1. **Toxicity of Traditional Passivation Systems**: Although traditional chromate passivation systems are effective, they contain highly toxic hexavalent chromium, which poses serious risks to human health and the natural environment. Therefore, developing chromium-free passivation technology is urgent. 2. **Improving the Corrosion Resistance of Passivation Films**: Existing silicate passivation films are environmentally friendly but lack sufficient corrosion resistance. The paper aims to improve the performance of silicate passivation films by adding organic components such as tannic acid, thereby enhancing their corrosion resistance. #### Research Methods: - **Passivation Formulation**: A specific passivation solution formula is used, including cobalt nitrate, sodium silicate, sodium citrate, and an appropriate amount of organic promoters. - **Passivation Treatment Process**: Zinc-iron alloy samples are prepared by electroplating and treated with both a conventional trivalent chromium passivation system and a self-prepared silicate passivation solution. - **Characterization and Testing**: Samples are characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), and electrochemical tests such as electrochemical impedance spectroscopy (EIS) and Tafel curves. #### Results and Discussion: - **Surface Morphology Analysis**: The surface of the untreated samples is rough with numerous dendritic structures; the surface after trivalent chromium passivation is relatively smooth but still has defects; the surface of the samples after silicate passivation is completely smooth and defect-free. - **Corrosion Resistance Testing**: The corrosion current density of the silicate passivation film is the lowest, indicating that it has the best corrosion resistance, superior to the trivalent chromium passivation film. In summary, this paper aims to develop a non-toxic silicate passivation system with good corrosion resistance to replace the traditional toxic chromate passivation system.