Trivalent chromium passivation for zinc coating and sealing of passivation film

Jian-zhong JIANG,Shu-ting MIU,Li-feng HAO,Sheng HAN

DOI: https://doi.org/10.3969/j.issn.1004-227X.2013.10.011

2013-01-01

Abstract:Zinc-plated tinplate was passivated using a selfdeveloped trivalent chromium passivation solution and sealed with silane. The composition of passivation solution are as follows: Cr2(SO4)3270 g/L, C6H8O7·H2O 10 g/L,CoSO4·7H2O 100 g/L, NH4HF277 g/L, NaH2PO2·H2O48.8 g/L, NaNO332 g/L, and sodium d-gluconate 15 g/L.The effects of passivation conditions such as temperature,pH, and time on the corrosion resistance of passivation film were discussed. The effect of vinyltrimethylsilane sealing on the surface morphology and corrosion resistance of passivation film was studied. The results showed that the passivation film obtained at room temperature and pH 1.8for 60 s on zinc coating has the best corrosion resistance,without white rust formation even immersed in 3.5% NaCl solution for 240 h. A uniform colloidal coating was formed on the passivation film after sealing with vinyltrimethylsilane, for which the time to formation of white rust in neutral salt spray test was extended from 95 h before sealing to 115 h, much longer than the industrial requirement(72 h).