Abstract:Hybrid laminates consist of layers of different materials, which determine the mechanical properties of the laminate itself. Furthermore, the structure and interfacial properties between the layers play a key role regarding the performance under load and therefore need to be investigated in respect to industrial applicability. In this regard, a hybrid laminate comprised of AA6082 aluminum alloy sheets and glass and carbon fiber-reinforced thermoplastic (polyamide 6) is investigated in this study with a focus on the influence of aluminum surface treatment application on tensile and fatigue behavior. Four different aluminum surface treatments are discussed (adhesion promoter, mechanical blasting, phosphating, and anodizing), which were characterized by Laser Scanning Microscopy. After the thermal consolidation of the hybrid laminate under defined pressure, double notch shear tests and tensile tests were performed and correlated to determine the resulting interfacial strength between the aluminum sheet surface and the fiber-reinforced plastic, and its impact on tensile performance. To investigate the performance of the laminate under fatigue load in LCF and HCF regimes, a short-time procedure was applied consisting of resource-efficient instrumented multiple and constant amplitude tests. Digital image correlation, thermography, and hysteresis measurement methods were utilized to gain information about the aluminum surface treatment influence on fatigue damage initiation and development. The results show that fatigue-induced damage initiation, development, and mechanisms differ significantly depending on the applied aluminum surface treatment. The used measurement technologies proved to be suitable for this application and enabled correlations in between, showing that the hybrid laminates damage state, in particular regarding the interfacial bonding of the layers, can be monitored not just through visual recordings of local strain and temperature development, but also through stress-displacement hysteresis analysis.

STUDY ON FATIGUE BEHAVIOR OF METAL/METAL LAMINATES

Micro Failure Analysis of Fiber Metal Laminates

About the Role of Interfaces on the Fatigue Crack Propagation in Laminated Metallic Composites

Delamination Behavior of an Advanced Al-Li Alloy Laminate During Fatigue Crack Growth

Fatigue crack propagation in explosive bonded LY12/20g double-layer metal laminate: I. Face-crack

In-situ investigation of deformation behavior and fracture forms of Ti/Al/Mg/Al/Ti laminates

An integrated computational and experimental study of the failure mode in Mg/Al laminated composite under three-point bending

Fatigue Life Optimized Layer Architecture of Ultrafine‐Grained Al–Ti Laminates Under Bending Stresses

Fatigue Crack Propagation in LY12/Cu Double-Layer Metal Laminate(ⅰ)——face-Crack

Study on Delamination Propagation Behavior and Measurement Method for One Kind of New Fiber Metal Laminates

Small fatigue crack propagation in Al-Cu alloy laminated structure via ultrasonic consolidation

Interlaminar Shear Strength Behavior of Carbon Fiber Reinforced Aluminum Alloy Laminate

De Lamination And Fatigue Crack Growth Behavior In Fiber Metal Laminates (Glare) Under Single Overloads

Investigation on shear and fatigue performance of CFRP/aluminum alloy single-lap adhesive joint

Fatigue behaviour of cracked steel plates reinforced with uhm cfrp laminate

Fatigue failure simulation of a double-lap composites-metal bolted joint structure

Influence of Aluminum Surface Treatment on Tensile and Fatigue Behavior of Thermoplastic-Based Hybrid Laminates

Crack Propagation and Debonding Development of CFRP Laminate Strengthened High-Strength Steel Plates under Fatigue Loadings

Influence of Interface on Mechanical Behavior of Al-B4C/Al Laminated Composites under Quasi-Static and Impact Loading

In-situ scanning electron microscopy studies of small fatigue crack growth in ultrasonic consolidation bonded aluminum 2024 laminated structure

Interlaminar mechanical properties of nano- and short-aramid fiber reinforced glass fiber-aluminum laminates: a comparative study