Fatigue crack propagation in explosive bonded LY12/20g double-layer metal laminate: I. Face-crack

Jianguo Cui,Jusheng Ma,Yonghui Fu,Nian Li,Jun Sun,JiaWen He

DOI: https://doi.org/10.3321/j.issn:0412-1961.2001.12.007

2001-01-01

Abstract:The fatigue face-crack growth behavior in explosive bonded double-layer metal composite plate (LY12/20g) was investigated. The results indicate that the elastic-plastic mismatch of components has significant influence on the near-tip "driving force" of fatigue crack growth. Specifically, the crack-tip is shielded from the remote loads when crack approaches the interface from the weaker material with lower yielding strength and elastic module.And the "effective driving force" at the crack tip is greater than the remote loads when crack approaches the interface from the stronger material with higher yielding strength and elastic module. The shielding and amplification on the near-tip "driving force" from the elastic-plastic mismatch between components are more and more obvious with the crack-tip approaching the interface. However, the effective ranges of elastic mismatch and plastic mismatch are not the same. The elastic mismatch acts from the fatigue crack starting growth to crack-tip contacting interface, and the strength mismatch only acts after the crack-tip plastic zone contacting the interface.