Fatigue behaviour of cracked steel plates reinforced with uhm cfrp laminate

Chao Wu,Xiao-Ling Zhao,Riadh Al-Mahaidi,Wenhui Duan

2010-01-01

Abstract:Composite materials have lead to great advances in improving fatigue performance of metallic structures over conventional strengthening methods. High modulus carbon fiber composites (CFRP) make this fatigue strengthening more promising by decreasing stress intensity factor of cracked metallic sections to a large extend. In this study, an ultra high modulus (UHM) CFRP laminate (with a modulus of 460 GPa) was adopted to strengthen initially cracked steel plates. A series of experiments was conducted to investigate the effectiveness of the composites on preventing fatigue crack propagation and extending the fatigue life of steel plates as well as the bond quality under fatigue effect. Two types of adhesives were used to bond UHM CFRP laminate onto steel surface to investigate the effects of adhesive properties. The adhesive thickness was varied to take into consideration of adhesive thickness effects. Five strengthening configurations were adopted by changing both the patch length and patch width. Both single-sided and double-sided repaired specimens were tested. During the fatigue tests the crack detection method of ‘‘beach marking” was adopted to record the crack propagation developing with fatigue cycles. Experimental results show that the application of UHM CFRP substantially reduces crack growth rate and prolongs fatigue life. Comparison with results of fatigue strengthening tests with CFRP sheets was also conducted. It was found that double-sided repair scheme is more efficient than single-patched scheme. Patch width and patch length have more considerable influence on the fatigue performance of repaired steel plates than patch configuration.