Abstract:Four examples of N,N-bis(aryl)butane-2,3-diimine–nickel(II) bromide complexes, [ArN=C(Me)-C(Me)=NAr]NiBr2 (where Ar = 2-(C5H9)-4,6-(CHPh2)2C6H2 (Ni1), Ar = 2-(C6H11)-4,6-(CHPh2)2C6H2 (Ni2), 2-(C8H15)-4,6-(CHPh2)2C6H2 (Ni3) and 2-(C12H23)-4,6-(CHPh2)2C6H2 (Ni4)), disparate in the ring size of the ortho-cycloalkyl substituents, were prepared using a straightforward one-pot synthetic method. The molecular structures of Ni2 and Ni4 highlight the variation in the steric hindrance of the ortho-cyclohexyl and -cyclododecyl rings exerted on the nickel center, respectively. By employing EtAlCl2, Et2AlCl or MAO as activators, Ni1–Ni4 displayed moderate to high activity as catalysts for ethylene polymerization, with levels falling in the order Ni2 (cyclohexyl) > Ni1 (cyclopentyl) > Ni4 (cyclododecyl) > Ni3 (cyclooctyl). Notably, cyclohexyl-containing Ni2/MAO reached a peak level of 13.2 × 106 g(PE) of (mol of Ni)−1 h−1 at 40 °C, yielding high-molecular-weight (ca. 1 million g mol−1) and highly branched polyethylene elastomers with generally narrow dispersity. The analysis of polyethylenes with 13C NMR spectroscopy revealed branching density between 73 and 104 per 1000 carbon atoms, with the run temperature and the nature of the aluminum activator being influential; selectivity for short-chain methyl branches (81.8% (EtAlCl2); 81.1% (Et2AlCl); 82.9% (MAO)) was a notable feature. The mechanical properties of these polyethylene samples measured at either 30 °C or 60 °C were also evaluated and confirmed that crystallinity (Xc) and molecular weight (Mw) were the main factors affecting tensile strength and strain at break (εb = 353–861%). In addition, the stress–strain recovery tests indicated that these polyethylenes possessed good elastic recovery (47.4–71.2%), properties that align with thermoplastic elastomers (TPEs).

Development of a Catalytic System for Synthesis of High Molecular Weight Polypropylene Elastomers

Synthesis and characterization of titanium(IV) complexes bearing end functionalized biphenyl: Efficient catalysts for synthesizing high molecular weight polyethylene

Preparation of Polyethylene Elastomers with Increased High Molecular Weight and Nearly Perfect Strain Recovery by Steric Control of Asymmetric Α-Diimine Nickel Catalyst

REMARKABLY ACTIVE NON-METALLOCENE ETHYLENE POLYMERIZATION CATALYSTS

Preparation of Polypropylene/MMT Nanocomposites Using Complex Supported Catalysts

Amorphous Elastomeric Ultra-High Molar Mass Polypropylene in High Yield by Half-Titanocene Catalysts

Propylene Polymerization to High Molecular Weight Atactic Polypropylene and Copolymerization with 1-Hexene Using Monocyclopentadienyl Titanium Catalysts.

Synthesis of High-Molecular-Weight Polypropylene Elastomer by Propylene Polymerization Using α-Diimine Nickel Catalysts

Propylene polymerization catalyzed by constrained geometry (cyclopentadienyl)phenoxytitanium catalysts

Synthesis of Ultrahigh Molecular Weight Ethylene-Based (co)polymers with Titanium Complexes Bearing Nonsymmetric Amine-bis(phenolate) Ligands

Ethylene–propylene Copolymerization with Bis(β‐enaminoketonato) Titanium Complexes Activated with Modified Methylaluminoxane

Highly active Ziegler-Natta Catalysts for propylene polymerization (2) effects of Al/Ti ratio and polymerization temperature

Studies on Synthesis of Low Isotactic Polypropylene by Using a Novel MgCl2-supported and Low Ti-loading Catalyst

N,N-Bis(2,4-Dibenzhydryl-6-cycloalkylphenyl)butane-2,3-diimine–Nickel Complexes as Tunable and Effective Catalysts for High-Molecular-Weight PE Elastomers

A Novel Catalytic System of [O,O] Bidentate Titanium Complexes and Et2AlCl/Bu2Mg for the Production of Ultra‐High Molecular Weight Polyethylene

Synthesis and performance of olefin copolymers produced with monocyclopentadienyl titanium phosphinimide complex as viscosity modifiers

Mechanistic Study on Effect of Electron Donors in Propylene Polymerization Using the Ziegler–Natta Catalyst

Ethylene/1-Octadecene Copolymerization Using [Eta(5):Eta(1)-C5me4-4-R-1-6-R-C6h2o]Ticl2 Catalysts

Synthesis of New Dendritic Titanium Catalysts and Catalytic Ethylene Polymerization

Study of the effect of the nature of catalyst systems on the molecular structure and properties of ultra-high molecular weight polyethylene

Ethylene/α‐olefin Copolymerization Using Diphenylcyclopentadienyl‐phenoxytitanium Dichloride/al(ibu)3/[ph3c][b(c6f5)4] Catalyst Systems