Cause Analysis of Longitudinal Crack on the Surface of Continuously Cast Slab

Xiaoguang Yang
2013-01-01
Abstract:In order to explore the cause of longitudinal crack in Lianyuan Steel,measurement and analysis are carried out on the quality of liquid steel,overheating degrees,inlet and outlet temperature of water,mould powder properties,surface fluctuation,and mould copper wall.The main reason is that: the high level of the sulfur content of some steels made w(Mn)/w(S) ratio 28.8;inlet temperature of water decreases to 25 ℃ after stop production,and then rapidly increases to 30-32 ℃ when production recovers.The basicity of mould powder changes fluctuate.Minimum value reaches 1.1,which leads to vitrification of powder and high heat conductivity.Surface fluctuation can reach as high as 6-7 mm,which leads to inflow inhomogeneity of mould powder and affects heat transfer.In addition,the scratch on the surface of mould copper wall results into defective contact,making the local temperature higher.The corresponding measures are put forward.The longitudinal crack rate of No.1 machine in Lianyuan Steel decreases from 0.50% to 0.024%.
What problem does this paper attempt to address?