Microstructure and Mechanical Property of Ti<sub>3</sub>AlC<sub>2</sub>/TiAl<sub>3</sub> Composite Synthesized by Hot Pressing

Wei Ping Chen,Yong Zeng,Xiao Mei Li,Hua Xiao
DOI: https://doi.org/10.4028/www.scientific.net/msf.816.210
2015-01-01
Materials Science Forum
Abstract:Ti 3 AlC 2 /TiAl 3 composite was successfully fabricated by ball milling and in-situ reaction/hot-pressing of Ti, Al and graphite powders mixture at 1200 °C and 30 MPa for 30 min. The phase composition and microstructure of the milled powders and synthesized composite were investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM), the mechanical properties and the toughening mechanism of 20%vol Ti 3 AlC 2 /TiAl 3 composite was also studied. The results show that no new phase is detected during 50 h of milling process. The in-situ synthesized samples are fully dense and composed of 72%vol TiAl 3 , 24%vol Ti 3 AlC 2 and 4%vol Al 2 O 3 /TiC. The Vickers Hardness, three-point bending strength and fracture toughness of the composite is ~5.2 GPa, ~243 MPa and ~4.3 MPa/m 1/2 , respectively. Analysis of microstructure reveals that crack deflection, crack bridging and delamination of Ti 3 AlC 2 are the main mechanism responsible for the toughening.
What problem does this paper attempt to address?