Preparation and mechanical properties of Ti2AlC/TiAl composites
WANG Wei,AI Tao-tao,FENG Xiao-ming,LI Wen-hu,JIANG Peng,YUAN Xin-qiang,BO Hai-wa,JING Ran
DOI: https://doi.org/10.13289/j.issn.1009-6264.2017.03.002
2017-01-01
Abstract:Ti2AlC/TiAl composites were fabricated by vacuum hot pressing technique in the Ti-Al-Ti3AlC2 system at 1100 ℃ for 1 h.Phase constituent and microstructure of the composites were analyzed by XRD,OM and SEM.The room temperature mechanical properties such as the density,Vickers hardness,flexural strength,compressive strength and fracture toughness were measured.The results reveal that the products are mainly composed of Ti3Al,Ti2AlC and TiAl phases.In situ Ti2AlC reinforcements developed by decomposition reaction of Ti3 AlC2 are mainly distributed in the matrix grain boundaries,part of which pinning in the intracrystalline.With the increase of Ti2AlC content,the agglomeration phenomenon aggravates gradually.The room temperature mechanical properties tests indicate that the mechanical properties of the Ti2 AlC/TiAl composites are obviously superior to the single-phase TiAl material.The Ti2 AlC/TiAl composites with 10 mass％ Ti3AlC2 additive presents better comprehensive performance,and the density,Vickers hardness,flexural strength,compressive strength and fracture toughness are 3.97 g/cm3,4.82 GPa,488.61 MPa,1340 MPa and 5.68 MPa·m1/2,respectively.The fracture mechanism of the Ti2AlC/TiAl composites is mixed with many kinds of fracture mode,including intergranular fracture,transgranular fracture,crack deflection and crack bridging.The toughening ways mainly include particulates-toughening,crack deflection and bridging toughening,and laminated-toughening.