Abstract:In this paper, dense MAX phase Ti3AlC2 enhanced and toughened TiAl3 matrix composites with mass fractions of 10∼40% were prepared by in-situ reaction via powder metallurgy route which using TiH2, Al and TiC powder as the starting materials. Then, the microstructure and phase structure of the composites were characterized, and the relationship between microstructure, mechanical properties and fracture mechanism was systematically investigated. The results show that the lath-like (micron level) and fine-needle-like (submicron level) reinforcements Ti3AlC2 are uniformly distributed in TiAl3 matrix. With the increases of mass fraction of reinforcements, the average grain size of the TiAl3 matrix decreases remarkably from 7.6 μm to 4.8 μm, indicating that the reinforcements Ti3AlC2 can effectively refine the matrix grains and plays a good pinning effect on the TiAl3 matrix. The prepared Ti3AlC2/TiAl3 composite with 30% mass fraction exhibits excellent comprehensive mechanical properties: the Vickers hardness, flexural strength, fracture toughness is 575 ± 5 HV, 470 ± 18 MPa, and 3.83 ± 0.05 MPa m1/2, 14.1%, 174.9% and 117.6% higher than that of the pure TiAl3 matrix, respectively. Both the strengthening and toughening effects are significant. The strengthening mechanism are fine grain strengthening and deformation strengthening, while the toughening mechanism is a synthetic effect in terms of crack deflection, crack bifurcation, grain refinement and stress-induced microcrack. Fracture analysis shows that the fracture mechanism is transgranular (cleavage) fracture.

Fabrication, microstructure and mechanical properties of TiAl matrix composite reinforced by submicro/nano-Ti 2 AlC

PREPARATION AND PROPERTIES OF TiB2/TiAl COMPOSITE SHEETS WITH LAYERED STRUCTURE

Balancing the strength and ductility of Ti2AlC/TiAl composite with a bioinspired micro-nano laminated architecture

Microstructure and Mechanical Properties of Ti2AlC-reinforced TiAl Composites

Fabrication, microstructure and compressive properties of Ti2AlC/TiAl composite with a bioinspired laminated structure

Microstructure and Mechanical Properties of Dual Scaled NbC/Ti2AlC Reinforced Titanium–Aluminum Composite

Hierarchically heterogeneous strategy for Ti 2 AlC/TiAl composite with superior mechanical properties

In-situ synthesized a dual-scale Ti 2 AlC reinforced TiAl composites with superior mechanical properties

In-situ TiC/Ti composites based on Ti 2 AlC–Ti system: Reaction process, microstructure, and mechanical properties

Tailoring Ultrafine Grained and Dispersion-Strengthened Ti2AlC/TiAl Composite Via a New Fabrication Route

Fabrication of Fully Dense Tial-Based Composite Sheets with A Novel Microlaminated Microstructure

Reaction mechanism and microstructure evolution of superhigh strength in-situ TiC/Ti composite based on Cr 2 AlC-Ti system

Preparation and toughness mechanism of in-situ Ti3AlC2 enhanced and toughened TiAl3 matrix composites

Microstructure, Mechanical Properties and Fracture Mechanism of Ti2AlC Reinforced AZ91D Composites Fabricated by Stir Casting

Preparation and characteristics of Ti3AlC2 -Al3Ti/Al composite materials synthesized from pure Al and Ti3AlC2 powders

Anisotropic microstructures and mechanical properties of textured Ti3AlC2/TiAl3/Al composite

Preparation of in situ TiC@TiN core–shell and Ti2N–Al4C3 nanoparticles and their effects on Al–Zn–Mg–Cu alloy

Microstructure characterization and enhanced mechanical properties of quasi-continuous network structured Ti3AlC2-Al3Ti/2024Al composite

Investigation on microstructure and properties of TiC0.5-Al2O3/Cu composites fabricated by a novel in-situ reactive synthesis

A novel way to fabricate high elastic modulus and high strength of TiC reinforced aluminum matrix composite

Microstructure, solidification behavior and mechanical properties of Al-Si-Mg-Ti/TiC fabricated by selective laser melting