Abstract:Black TiO2−x is an attractive material due to its adjustable band structure, useful in different applications, and has been heavily investigated and developed. The current reduction of TiO2 involves a process from surface to center: thus, the issue of either insufficient or excessive reduction seems inevitable. To the best of our knowledge, it is rarely reported that a homogeneous defect distribution can be facilely achieved inside black TiO2−x. In this study, a bulk-reduced rutile TiO2−x was obtained via a circuitous two-step approach, with an intermediate Magneli phase (TinO2n−1). With the decomposition of a solid atmosphere creator (e.g. KClO4 grains) at a high temperature, the missing oxygen ions in Ti4O7 could be replenished quantitatively. The TEM and SAED results reveal that the oxidation process is not just a surface reaction, but it involves reverse displacement or structural rearrangement inside the crystal. In particular, the periodic variation of crystallographic sheer planes was the direct evidence of the above bulk reaction, i.e. unified long period for Ti4O7 and varied long period for critical ratio sample. The as-prepared samples showed different band gaps and colors, based on their oxygen content. KClO4, with a critical mixing ratio of around 17.5 mol%, could almost oxidize Ti4O7 to black rutile TiO2−x. Furthermore, the sample formed at the critical ratio showed a considerable photo-thermal response speed of 1.7 °C s−1 and an equilibrium temperature of up to 70 °C under irradiation with light above 400 nm, which can be an evidence for the enhancement of non-intrinsic absorption. In short, this study provides a new route for the controllable preparation of black TiO2−x, and a possibility for further development of other solid atmosphere creators.

One-Step Solvothermal Synthesis of Black TiO<SUB>2</SUB> Films for Enhanced Visible Absorption

Controllable Hydrothermal Synthesis, Optical and Photocatalytic Properties of TiO2 Nanostructures

APPLICATION AND OPTICAL PROPERTIES OF TiO_2 THINFILMS PREPARED BY CHEMICAL VAPOUR DEPOSITION

Black TiOx Films with Photothermal-Assisted Photocatalytic Activity Prepared by Reactive Sputtering

Preparation of TiOx-C Nano-Composite Films as Solar Selective Absorbers by Sol-Gel Method

Synthesis of Black TiOx Nanoparticles by Mg Reduction of TiO2 Nanocrystals and Their Application for Solar Water Evaporation

Synthesis of Black TiO2 with Efficient Visible-Light Photocatalytic Activity by Ultraviolet Light Irradiation and Low Temperature Annealing

Preparation of nanoscaled TiO 2 films with high visible light photocatalytic activity at low temperature

Progress in Black Titania: A New Material for Advanced Photocatalysis

A Facile Approach to Prepare Black TiO2 with Oxygen Vacancy for Enhancing Photocatalytic Activity

Tuning of Electrical and Optical Properties of Tantalum Doped TiO2 Flims Prepared by Sol-gel Method

Controllable preparation of black titanium dioxide and its wave-absorbing properties

Building Architecture of TiO2 Nanocrystals Embedded in Amorphous WO3 Films with Improved Electrochromic Properties

A Safe and Efficient Approach to Fabricate Black Carbon-Doped Rutile Titania by Substitution of Oxygen at Carbon Sites in Titanium Carbide Film

Hydrophilicity and Photocatalysis of Ti1−xVxO2 Films Prepared by Sol–gel Method

Strong Saturable Absorption of Black Titanium Oxide Nanoparticle Films

Low-temperature fabrication of brown TiO2 with enhanced photocatalytic activities under visible light

Engineering black titanium dioxide by femtosecond laser filament

A Reverse Slipping Strategy for Bulk-Reduced TiO2−x Preparation from Magnéli Phase Ti4O7

Visible absorbing TiO2 thin films by physical deposition methods

Recent Advances in Black TiO2 Nanomaterials for Solar Energy Conversion

One-Step Solvothermal Synthesis of Black TiO&lt;SUB&gt;2&lt;/SUB&gt; Films for Enhanced Visible Absorption