Abstract:The band gap of rutile TiO2 has been narrowed, via the formation of oxygen vacancies (OVs) during heat treatment in carbon powder (cHT) with embedding TiO2 coatings. The narrowed band gap efficiently improves the visible light response of TiO2 coatings, to further enhance the visible-light-driven photocatalytic activity. The change in OVs during cHT has been studied by manipulation of cHT temperature and time. The effect of OVs on the band structure of nonstoichiometric TiO2-x has been further calculated by first-principles calculations. With raising the temperature, SEM images show that the nano-size fiber-like structure forms on the surface of TiO2 coatings, and the amount of the fiber-like structure significantly increases and their size changes from nano to micro under 800 °C, contributing to cause an increase in accessible surface area. The UV-Vis results reveal that the band gap of TiO2 has been narrowed during cHT, due to the formed oxygen vacancies. The XPS results further confirm that the formation of surface defects including OVs, and the XPS depth profile further shows the decreased relative amount of O whereas increased relative amount of carbon. Notably, after cHT for TiO2 coatings, the photocatalytic activity first increases then decreases with raising the temperature, achieving approximately 3 times at 850 °C. The first-principles calculation suggest that the OVs in TiO2 coatings with localized electrons could facilitate the band gap narrowing, further favoring to enhance the photocatalytic activity under visible light.

A Safe and Efficient Approach to Fabricate Black Carbon-Doped Rutile Titania by Substitution of Oxygen at Carbon Sites in Titanium Carbide Film

Facile Fabrication of N-doped TiO2 Nanocatalyst with Superior Performance under Visible Light Irradiation

Fabrication of Oxygen-Deficient TiO 2 Coatings with Nano-Fiber Morphology for Visible-Light Photocatalysis

Carbon-Doped Anatase Tio2 Obtained from Tic for Photocatalysis under Visible Light Irradiation

The Fabrication and Characterization of Novel Carbon Doped TiO2nanotubes, Nanowires and Nanorods with High Visible Light Photocatalytic Activity

Fabrication of V-Doped TiO2 Nanoparticles and Photocatalytic Studies under Visible Light

Black TiOx Films with Photothermal-Assisted Photocatalytic Activity Prepared by Reactive Sputtering

Investigation of structure and properties of N-doped TiO2 thin films grown by APCVD

Role of carbon in titania as visible-light photocatalyst prepared by flat-flame chemical vapor condensation method

Preparation and Properties of N -Doped TiO2 Films by APCVD

Microstructures and Properties of N-Doped TiO_2 Films Grown by Atmospheric Pressure Chemical Vapor Deposition

P-doped TiO_2 Immobilized Diatomite and Its Photocatalytic Performance under Visible Light

Enhanced Optical Absorption and Photocatalytic Activity of Cu/N-Codoped Tio2 Nanocrystals

Carbon-doped γ-Ti3O5 film with enhanced photothermal conversion performance

Multi-type Carbon Doping of TiO2 Photocatalyst

Nanostructured Carbon-Doping Anodic Tio2 From Tic And Its Photoelectrochemical Properties

Significantly Enhanced Photocatalytic Activity of TiO2/TiC Coatings under Visible Light

Enhancement of the visible light photocatalytic activity of C-doped Tio2 nanomaterials prepared by a green synthetic approach

Facile Synthesis of Anatase–Rutile Diphase N-doped TiO2 Nanoparticles with Excellent Visible Light Photocatalytic Activity

Degradative and disinfective properties of carbon-doped anatase-rutile TiO2 mixtures under visible light irradiation

Oxygen vacancies induced band gap narrowing for efficient visible-light response in carbon-doped TiO2