Abstract:Due to the randomness of hard and brittle material damage evolution, assessing damage and interpreting mechanisms is challenging. This study focuses on analyzing material damage mechanisms by employing extensive multi-source heterogeneous data to extract quantitative information. A machine vision-based method for detecting and assessing defects in ceramics was proposed, achieving 98 % accuracy. Leveraging this method in scratching experiments, the progression of damage and micro-failure mechanisms in Si3N4 was investigated through the analysis of defect area distribution, force and acoustical signals. Results revealed that the distribution of defect areas conforms to a three-parameter Weibull distribution. At scratch depths of 0.01, 0.02 mm, approximately 90 % of damage accumulated within 1e2–1e4 μm 2 ; conversely, 0.03–0.06 mm led to a decrease to 30 – 40 %. Extensive crack propagation occurs within 0.02–0.03 mm, resulting in the intersecting formation of spalling blocks. Damage evolution occurs in three stages: shallow and small cracks with scattered spalling blocks in the first stage, deep and long cracks with continuous and irregularly shaped spalling blocks in the second stage, and nearly no cracks with continuous and regularly shaped blocks in the third stage. This study not only proposes an efficient method to detect and evaluate ceramic defects, but also deeply understands the evolution process of material damage mechanism. Considering defect distribution and statistical trends, this research not only provide guidance for the optimization of machining parameters, especially in the scene of specific precision and high removal rate. At the same time, the damage evolution and failure mechanism of Si 3 N 4 provide useful experimental basis and data support for deepening the understanding of material behavior during ultra-precision grinding.

A Coupled 3d Morphological Reconstruction Approach for Surface Microcrack in Si3n4 Ceramic Bearing Roller Based on Adaptive Nano Feature Extraction & Multiscale Depth Fusion

A coupled 3D morphological reconstruction method for point microcrack defects in Si 3 N 4 ceramic bearing rollers

Extraction method for characterizing microcracks on Si3N4 ceramic bearings rolling element with contour segmentation

Surface Crack Identification on a Cylinder Using the Signal Enhancement of the Scanning Laser Line Source Method

Study on the Model of Surface Crack Depth in Ceramics Grinding

Numerical Study for Surface-breaking Crack Detection on A Cylinder Using Laser-generated Ultrasound

Method of Damage Characterization of Engineering Ceramics Grinding Surface

Evaluation and Measurement of Surface/Subsurface Crack Damage of Ground Ceramics

A Study on 3D Micro-Topographical Measurement of FRCMC Grinding Surface

A method for multi-view surface defect detection of Si 3 N 4 ceramic bearing balls integrating features enhanced by the Gabor salient domain

The edge artifact extraction method for Si3N4 ceramic bearing rolling element microcracks characterization

Quantification of micro-damage evolution process in ceramics through extensive analysis of multi-source heterogeneous data

Evaluation on Ground Surface Accuracies of Large-Depth and Steeply Micro-Structured SiC Surfaces

Identification of Subsurface Mesoscale Crack in Full Ceramic Ball Bearings Based on Strain Energy Theory

Automatic detection and pixel-level quantification of surface microcracks in ceramics grinding: An exploration with Mask R-CNN and TransUNet

Microcrack Initiation and Propagation in 3C-SiC Ceramic Based on Molecular Dynamics Nano-Drilling

Study of Prefabricated Crack Propagation on Monocrystalline Silicon Surfaces for Grinding Damage Analysis

A fault diagnosis method based on stiffness evaluation model for full ceramic ball bearings containing subsurface cracks

Comparative Study on Surface Contact Fatigue of Machine Tool Bearing Raceways with Different Rolling Elements: Two Failure Bearings Case Studies

Micro-milling of Fused Silica Based on Instantaneous Chip Thickness

Experimental Analysis and Modelling of C-Crack Propagation in Silicon Nitride Ball Bearing Element under Rolling Contact Fatigue