Abstract:The joining of C f /C composite to Mo30Cu alloy plays an important practical role in a bias filter for thermonuclear fusion. In this study, the C f /C composite is joined to Mo30Cu alloy at 860 °C/10 min using AgCu4.5Ti braze after fabricating the three dimensional (3D) heat transfer interface along the C f /C interface. The effect of interface grooving on the thermal conductivity of the joint is investigated and compared with the original brazed joint. The results demonstrate that the room temperature thermal conductivity of the joint reached a maximum of 132 W·m −1 ·K −1 at a grooving depth of 200 μm, which is 17.8 % higher than that of the original joint (112 W·m −1 ·K −1 ). The thermal conductivity of the joint is still as high as 100 W·m −1 ·K −1 at a temperature of 500 °C. The excellent high-temperature thermal conductivity significantly reduces the C f /C damage and extends the service life of the joint. And the shear strength of the joint has also been significantly increased by 252 % from 13.1 MPa to 33.1 MPa. Grooves prepared along the C f /C interface provide channels for braze penetration, increasing the contact area between the brazing seam and the C f /C matrix. Ultimately, the thermal evacuation performance of the joint is improved by increasing the heat exchange area across the joint. Also, grooves along the C f /C interface enable mechanical interlocking with the brazing seam, achieving an enhanced joint strength. The heat transfer process of the brazed joint is simulated and analyzed by the finite element method. The analysis indicated that the thermal evacuation across the joint can be enhanced by pre-fabricating a 3D heat transfer interface in the joint. This research can provide a reference for solving the problem of heat accumulation in the first wall materials inside thermonuclear reactors.

Enhancing the High-Temperature Thermal Evacuation of Cf/C-Mo30Cu Joint Via Grooving 3D Heat Transfer Interface

Enhancing the high-temperature thermal evacuation of C f /C-Mo30Cu joint via grooving 3D heat transfer interface

Achieving high-temperature thermal evacuation between dissimilar materials C f /C and Mo30Cu by forming a brazed joint

Achieving High-Temperature Thermal Evacuation Between Dissimilar Materials Cf/C and Mo30Cu by Forming a Brazed Joint

Achieving High-Thermal-conductivity Brazed Joint Between Carbon-Based Composites and Mo-Cu Alloys by Increasing the Heat Transfer Area

Tungsten Joining with Copper Alloy and Its High Heat Load Performance

Achieving High Thermal Conductivity Joining of Cf/C and Haynes 230 by Using Cu-Mo30Cu-Ti Composite Foil As Thermal Interface Material

Thermal fatigue failure behavior on Be/Cu joint of ITER first wall after enhanced heat flux test

Achieving high thermal conductivity joining of C f /C and Haynes 230 by using Cu-Mo30Cu-Ti composite foil as thermal interface material

Exploring the Role of Liquid Braze Filling the Dissimilar Cf/C-Haynes 230 Joint to Enhance the Interfacial Heat Transfer

Microstructure evolution and improved mechanical strength of the C/C-Mo joint by adjusting the joining temperature in a wide temperature range

Pre-infiltration and brazing behaviors of Cf/C composites with high temperature Ti Si eutectic alloy

Directly Construct a Gradient Brazed Joint of SiCf-SiC and Ni-based Superalloy Using a High-Temperature AuCuV Filler

Investigating the Role of Surface Contact Area Adjustment for Enhancing Interfacial Heat Transfer of the Cf/C-Haynes 230 Joint

Interfacial Strengthening Mechanism of C/C/Nb0.74CoCrFeNi2/Nb Brazed Joints: Stress-relieving Effects of the FCC Phase

Ultra-high Temperature Brazing of C/C Using a Simplified FeNiCrCu High-Entropy Alloy As Filler

High temperature brazing of C/C using Hastelloy C-276 as filler and joint formation mechanism

Interfacial Microstructure and Mechanical Properties of C/C Composites and Nb Joints Brazed with Cu75Pt25 Filler Metal

Microstructural evolution and mechanical property of a SiCf/SiC composite/Ni-based superalloy joint brazed with an Au-Cu-Ti filler

Vacuum brazing of C/C composite to TC4 alloy using nano-Al 2 O 3 strengthened AgCuTi composite filler

Vacuum Brazing of the C-f/C Composite and Ni Base Superalloy Using MBF 20 Filler