Abstract:To further the anti-ablation property of carbon/carbon composites (C/Cs) at extreme-high temperature, Cr-ZrC coating is fabricated on SiC-coated C/Cs. The anti-ablation properties of the ZrC coatings modified by various content of Cr are tested by oxyacetylene flame (heat flux: 2.4 MW/m(2)). Compared with pure ZrC coating, the ablation resistance property of the sprayed Cr-ZrC coating indicates an effective improvement. Cr acts as an accelerant by facilitating the liquid ZrO2 sintering and form a close structure. This dense structure can alleviate oxygen penetration. As the content of Cr increase (10 wt%, 15 wt% and 20 wt%), after cooling can also detect the retaining of tetragonal-ZrO2 (t-ZrO2). The phase transformation from t-ZrO2 to monoclinic ZrO2 (m-ZrO2) can lead to the volume expansion. The retaining of t-ZrO2 shows the phase transformation is impeded, which contributes to the thermal stability of the Cr modified ZrC coating. In the specimen, oxygen mainly diffuse through micropores, microcracks and grain boundaries. For Cr-ZrC coating, these diffuse ways could be partly or completely sealed by melted Zr-O-Cr coating during ablation test, which can effectively protect C/Cs during the oxyacetylene ablation test. When the content of Cr is 15 wt%, on the surface can form dense dendritic structure, which can effectively protect C/Cs from ablation.

Effect of SiC Nanowires on Ablation Property of Cu-doped C/C-ZrC Composites

Fabrication and Ablation Properties of SiC Nanowires-Network Modified Carbon/Carbon–Ultrahigh Temperature Ceramics Composites

The Ablation Behavior and Mechanical Property of C/C-SiC-ZrB2 Composites Fabricated by Reactive Melt Infiltration

Ablation Behaviors and Mechanism of ZrC-SiC-Si/SiC-Si Double-Layered Coatings on C/C Composite under Plasma Flame at 3000 °C

Preparation and Ablation Properties of SiC Nanowire-Reinforced ZrC–SiC Coating-Matrix Integrated C/C Composites

Ablation Behaviors of SiC Nanowire-Reinforced ZrC-SiC Coating-Matrix Integrated C/C Composites with Different Ratios of Precursors

Effect of CVI SiC Content on Ablation and Mechanism of C/C-SiC-ZrC-Cu Composites

Effect of SiC/ZrC Ratio on the Mechanical and Ablation Properties of C/C–SiC–ZrC Composites

SiC Nanowire Toughened ZrB2–SiC Ablative Coating for SiC Coated C/C Composites

Effect of temperature-dependent nano SiC on the ablation resistance of ZrC coating

Enhanced Anti-Ablation Performance of Carbon/carbon Composites Modified with ZrC-SiC

Effects of ZrC/SiC Ratios on Mechanical and Ablation Behavior of C/C–ZrC–SiC Composites Prepared by Carbothermal Reaction of Hydrothermal Co-Deposited Oxides

Effect of Al2O3 Addition on the Ablation Behavior of SiC-ZrC Coated C/C Composites

Preparation, Ablation Behavior and Mechanism of C/C-ZrC-SiC and C/C-SiC Composites

Local Anti-Ablation Modification of Uneven-Density C/C Composites with the ZrC-SiC Composite Ceramics

Thermal ablation behavior of SiC coating for 3D braided carbon fiber reinforced ZrC-SiC composites in different heat fluxes

Microstructure and High Temperature Anti-Ablation Behavior of Cr-modified ZrC Coating for SiC-coated Carbon/carbon Composites

Effect of In-Situ Grown SiC Nanowires on the Mechanical Properties of HfC-ZrB2-SiC Modified C/C Composites

Investigation on Ablation Characteristics of C/C Composites with ZrC/SiC Coating

Effect of ZrC–SiC Content on Microstructure and Ablation Properties of C/C Composites

Microstructure and Ablation Behavior of SiC Coated C/C–SiC–ZrC Composites Prepared by a Hybrid Infiltration Process