Abstract:In this study, C/C–SiC and C/C–SiC–ZrC composites were prepared via chemical vapor infiltration and polymer infiltration pyrolysis, and the ablation mechanism under hypersonic oxygen-rich environmental conditions was investigated. The C/C–SiC composites demonstrate an excellent ablation resistance in a hypersonic oxygen-rich environment with a relatively low temperature and speed of approximately 1800 K and 1100 m/s, respectively. It is only in the ablation center area with higher temperatures that a certain degree of thermochemical ablation was observed. The mass and linear ablation rates of C/C–SiC composites (0.027 g/s and 0.117 mm/s, respectively) showed a significant increase in a hypersonic oxygen-rich environment with a temperature and velocity of approximately 2050 K and 2000 m/s, respectively. The high-temperature ablation resistance of ZrC-modified C/C–SiC–ZrC composites improved significantly. However, the ZrC ceramic component had a considerable impact on the ablation resistance of the material. The structural integrity of C/C–20SiC–30ZrC composites was relatively high in hypersonic oxygen-rich environments with a jet temperature and velocity of 2050 K and 2000 m/s, respectively, and mass and linear ablation rates were 0.012 g/s and 0.015 mm/s, respectively. When the ZrC content increased by 40%, the ablation resistance of the composite reduced significantly, whereas the mass and linear ablation rates increased to 0.043 g/s and 0.130 mm/s, respectively.

Effect of CVI SiC Content on Ablation and Mechanism of C/C-SiC-ZrC-Cu Composites

Ablation Behaviors and Mechanism of ZrC-SiC-Si/SiC-Si Double-Layered Coatings on C/C Composite under Plasma Flame at 3000 °C

Effect of ZrC–SiC Content on Microstructure and Ablation Properties of C/C Composites

The Ablation Behavior and Mechanical Property of C/C-SiC-ZrB2 Composites Fabricated by Reactive Melt Infiltration

Preparation, Ablation Behavior and Mechanism of C/C-ZrC-SiC and C/C-SiC Composites

Ablative Property and Mechanism of SiC-CuxSiy Modified C/C-ZrC Composites Prepared by a Rapid Method

Ablation Performances of Multi-Phased C/C-Zrc-Sic Ultra-High Temperature Composites

Mechanical, Oxidation and Ablation Properties of C/(C-SiC)CVI-(ZrC-SiC)PIP Composites

Effect of SiC coating on ablation resistance of C/C composites under oxyacetylene torch flame

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Effect of Reaction Melt Infiltration Temperature on the Ablation Properties of 2D C/C–SiC–ZrC Composites

Ablation Behavior of ZrC–SiC Coated C/C–ZrC–SiC Composites Prepared by Precursor Infiltration Pyrolysis Combined with Reactive Melt Infiltration

Enhanced Anti-Ablation Performance of Carbon/carbon Composites Modified with ZrC-SiC

Oxidation And Ablation Resistance Of C-F/Zrc-Sic Ultra-High Temperature Composites

Microstructure and Ablation Property of C/C-ZrC-SiC Composites Fabricated by Chemical Liquid-Vapor Deposition Combined with Precursor Infiltration and Pyrolysis

Processing and Ablation Properties of C/SiC-(W-C) Composites

Ablation Behavior of C/C-ZrC-SiC Composites Prepared by Reactive Melt Infiltration under Oxyacetylene Torch at Two Heat Fluxes

Ablation Behavior and Mechanism of C/C–ZrC–SiC Composites under an Oxyacetylene Torch at 3000°C

Microstructure and Ablation Behavior of SiC Coated C/C–SiC–ZrC Composites Prepared by a Hybrid Infiltration Process

Ablation mechanism of C/C–SiC and C/C–SiC–ZrC composites in hypersonic oxygen-enriched environment

Ablation Property and Mechanism of ZrC-Cu-C/C Composites