Abstract:In this study, C/C–SiC and C/C–SiC–ZrC composites were prepared via chemical vapor infiltration and polymer infiltration pyrolysis, and the ablation mechanism under hypersonic oxygen-rich environmental conditions was investigated. The C/C–SiC composites demonstrate an excellent ablation resistance in a hypersonic oxygen-rich environment with a relatively low temperature and speed of approximately 1800 K and 1100 m/s, respectively. It is only in the ablation center area with higher temperatures that a certain degree of thermochemical ablation was observed. The mass and linear ablation rates of C/C–SiC composites (0.027 g/s and 0.117 mm/s, respectively) showed a significant increase in a hypersonic oxygen-rich environment with a temperature and velocity of approximately 2050 K and 2000 m/s, respectively. The high-temperature ablation resistance of ZrC-modified C/C–SiC–ZrC composites improved significantly. However, the ZrC ceramic component had a considerable impact on the ablation resistance of the material. The structural integrity of C/C–20SiC–30ZrC composites was relatively high in hypersonic oxygen-rich environments with a jet temperature and velocity of 2050 K and 2000 m/s, respectively, and mass and linear ablation rates were 0.012 g/s and 0.015 mm/s, respectively. When the ZrC content increased by 40%, the ablation resistance of the composite reduced significantly, whereas the mass and linear ablation rates increased to 0.043 g/s and 0.130 mm/s, respectively.

Effect of SiC/ZrC Ratio on the Mechanical and Ablation Properties of C/C–SiC–ZrC Composites

Effects of ZrC/SiC Ratios on Mechanical and Ablation Behavior of C/C–ZrC–SiC Composites Prepared by Carbothermal Reaction of Hydrothermal Co-Deposited Oxides

Microstructures and Ablation Properties of C/C−SiC−ZrC Composites Prepared Using C/C Skeletons with Various Densities

Effect Of Zrc Amount And Distribution On The Thermomechanical Properties Of C-F/Sic-Zrc Composites

The Ablation Behavior and Mechanical Property of C/C-SiC-ZrB2 Composites Fabricated by Reactive Melt Infiltration

Effect of C/C density on the properties of C/C-SiC-ZrC composites

Effects of Porous C/C Density on the Densification Behavior and Ablation Property of C/C–ZrC–SiC Composites

Effects of preform structures on the mechanical and ablation properties of C/ZrC-SiC composites

Influence of ZrC Content on Mechanical Properties of C/C- ZrC Composites

The mechanical properties of C/C-ZrC-SiC composites after laser ablation

Effect of SiC Nanowires on Ablation Property of Cu-doped C/C-ZrC Composites

Mechanical Properties and Ablation Behavior of C/C-ZrC and C/C-ZrC-SiC Composites Prepared by Precursor Infiltration and Pyrolysis Combined with Chemical Vapor Infiltration

Effect of ZrC–SiC Content on Microstructure and Ablation Properties of C/C Composites

Enhanced Anti-Ablation Performance of Carbon/carbon Composites Modified with ZrC-SiC

Microstructure and Ablation Performance of SiC–ZrC Coated C/C Composites Prepared by Reactive Melt Infiltration

Ablation Behaviors of SiC Nanowire-Reinforced ZrC-SiC Coating-Matrix Integrated C/C Composites with Different Ratios of Precursors

Ablation Resistance of SiC–HfC–ZrC Multiphase Modified Carbon/carbon Composites

Preparation, Ablation Behavior and Mechanism of C/C-ZrC-SiC and C/C-SiC Composites

Ablation mechanism of C/C–SiC and C/C–SiC–ZrC composites in hypersonic oxygen-enriched environment

Ablation Resistance of SiC–ZrC Coating Prepared by a Simple Two-Step Method on Carbon Fiber Reinforced Composites

Oxidation And Ablation Resistance Of C-F/Zrc-Sic Ultra-High Temperature Composites