Abstract:To refine microstructure, adjust the ratio of gamma/alpha(2) and improve the mechanical properties, Ti46Al 2.6 C-xNb (at. %) alloys were prepared by arc melting under the action of ultrasound. The phase composition, lamellar colony size, elements distribution, the kinds and distribution of carbides and compressive properties were investigated. Results show that as the Nb content increases, the relative content of alpha(2) phase and Ti2AlC phase increases, and the relative content of gamma phase decreases. TiC phase completely reacts to form Ti2AlC phase and its shape changes from coarse long rod to short rod. The microstructure was refined with the addition of Nb under ultrasound treatment. Lamellar colony size decreases from 36.9 to 21.5 mu m, lamellar spacing decreases from 1.6 to 0.8 pm, and the length-diameter ratio of Ti2AlC decreases from 5.4 to 4.0 when the Nb content increases from 0 to 8.0 at. %. During solidification process, not only the component supercooling and heterogeneous nucleation of Nb are increased, but also the crystal grains are broken and the nucleation barrier is reduced under the action of ultrasound to promote the nucleation. The microstructure is refined and the uniformity of the element distribution is improved. Compressive results show that the strength increases from 2074.1 to 2474.2 MPa and the strain increases from 23.4% to 28.0% when the Nb content increases from 0 to 4 at. %. The refinement of lamellar colony and Ti2AlC, the ratio of gamma/alpha(2 )and solid-solution of Nb are the main reasons for improving compressive properties. (C) 2022 Elsevier B.V. All rights reserved.

Mechanism of Interstitial Atoms on Oxidation and Fracture of Niobium-Silicon Alloys

Optimization of Zr and Mo element on room-temperature fracture toughness and the integrity of oxide film

Mechanical Properties and Oxidation Characteristics of TiNiAl(Nb) Intermetallics

Effect of Trace Boron Addition on the Microstructural Evolution and Mechanical Properties in Ti45al8nb2cr-B Alloys

A Study on Fine Nbss/γ-(Nb,X)5Si3 Eutectic with Significantly Improved Room-Temperature Fracture Toughness by Added ZrB2

Microstructure and Fracture Toughness of Nb-Si Based Alloys by with Ti, Zr and Hf Additions

Effects of Niobium and Ultrasonic Action Coupling on Microstructure Evolution and Mechanical Properties of Ti46Al2.6 C Alloy

Effect of Ni on Microstructures and Mechanical Properties for Multielemental Nb–Si-Based Alloys

Study on the Oxidation Behavior of TiB2-CeO2-Modified (Nb,Mo,Cr,W)Si2 Coating on the Surface of Niobium Alloy

Improving the mechanical properties and oxidation resistance of Nb-16Si-20Ti alloys with B 4 C addition

Microstructure Evolution and Mechanical Properties of ZrC-added Nb–16Si–20Ti Alloys

The Effects of Nb Content on Microstructure and Fracture Behavior of Near Α Titanium Alloys

Synergistic Effect of Zr and Ti on Microstructure and Properties for Nb Si Based In-Situ Composites

Effects of the microstructure and minor elements on the fracture toughness of Nb-Si alloy

Microstructure and oxidation behavior of Nb-based multi-phase alloys

Effects of Niobium on Phase Composition and Improving Mechanical Properties in TiAl Alloy Reinforced by Ti2AlC

Mo effect on the phase stability and room-temperature fracture toughness of Nb/Nb5Si3 in-situ composites

Cooperative Effects of Mo and B Additions on the Microstructure and Mechanical Properties of Multi-Elemental Nb-Si-Ti Based Alloys

Synergistic Effects of Fe and C on Microstructure and Properties of Nb-Ti-Si Based Alloys

On the oxidation mechanism of niobium-base in situ composites

Synchronous improvement in room-temperature fracture toughness and high-temperature oxidation resistance of Nb Si based alloys with Erbium addition