Synchronous improvement in room-temperature fracture toughness and high-temperature oxidation resistance of Nb Si based alloys with Erbium addition

Yu Wang,Lina Jia,Guangxin Sun,Fengxiang Zhang,Chengtong Ye,Hu Zhang
DOI: https://doi.org/10.1016/j.ijrmhm.2020.105359
IF: 4.804
2021-01-01
International Journal of Refractory Metals and Hard Materials
Abstract:<p>The microstructure, room-temperature fracture toughness and high-temperature oxidation resistance of Nb-16Si-23Ti-4Cr-2Al-2Hf-xEr (x = 0, 0.1, 0.4, 0.6, at.%) alloys via directional solidification and heat treatment were investigated. Results showed that all the alloys consisted of Nb<sub>ss</sub>, αNb<sub>5</sub>Si<sub>3</sub> and γNb<sub>5</sub>Si<sub>3</sub> phase, Er addition refined the microstructure, increased the volume fraction and continuity of Nb<sub>ss</sub> matrix. Since the high-activity of Erbium, it is in-situ oxygenated to form a mixed oxide phase in the form of discreet particles, alloy melt got purification by internal oxidation mechanism. The higher density dislocations which may be induced by thermal expansion mismatch were piled up around the oxide particle compared with other regions in Nb<sub>ss</sub> matrix. Er-doping contributed to eliminate segregation of Ti and then reduced its concentration-sensitive effect. Besides, more Nb<sub>ss</sub>/silicide interface decohesion was triggered by addition of Er. So the 0.4 at.% Er addition significantly enhanced the fracture toughness of NbSi based alloys from 8.4 MPa·m<sup>1/2</sup> to 24.5 MPa·m<sup>1/2</sup> at room temperature. Er also accelerated the formation of complex oxide products and transition from linear oxidized regularity to parabolic, and obviously decreased the weight gain from 258.2 mg/cm<sup>2</sup> to 164.3 mg/cm<sup>2</sup> after oxidation at 1300 °C for 100 h.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?