Abstract:The 347H austenitic stainless steel has been widely used for pressure vessels and pipeline (PVP) applications due to its excellent creep and corrosion resistance, which fit ideally to the harsh conditions in petrochemical industries, fossil fuel or nuclear power plants, and modern energy storages. However, a failure mode has been commonly observed with cracks emerging at the heat affected zone (HAZ) of weldments during post-weld heat treatment (PWHT) or under intermediate to high temperature service conditions. This phenomenon is termed as Stress Relaxation Cracking (SRC) since the purpose of PWHT is to relieve the welding-induced residual stress fields, or as Stress Age Cracking (SAC) if failure happens during service. A leading literature explanation of this failure suggests that the residual stress relaxation and the precipitation dissolution and/or re-precipitation occur in the same temperature range, which can lead to locally high strains and thus to crack at the grain boundaries. Since in situ spatial measurements of residual stress fields, microstructural evolution, and failure processes are nearly infeasible, this work recourses to a micromechanical finite element framework that models the high temperature failure as the nucleation and growth of grain boundary cavities, whereas various parameters such as thermomechanical loading history and its evolution, the competition of grain-interior dislocation creep and grain-boundary diffusion in failure lifetime, and microstructural heterogeneities (such as the precipitate free zone near grain boundaries) can be quantitatively incorporated. It can be concluded from these microstructure-explicit simulations that an accurate knowledge of residual stress evolution and a carefully calibrated set of material constitutive parameters are the essential prerequisites for lifetime predictions. The understanding of individual governing factors also leads to a mechanistic interpretation of the observed SRC susceptibility C-curves. These results suggest that the criticality of residual stress evolution, but not the precipitation-induced local strains, be the leading factor for SRC.

Investigating the Thermal Stability of Compressive Residual Stress in a Gradient Nanostructured Austenitic Stainless Steel by In-Situ Xrd and Tem

Strain-induced Refinement and Thermal Stability of a Nanocrystalline Steel Produced by Surface Mechanical Attritiontreatment

Controllable Martensite Transformation and Strain-Controlled Fatigue Behavior of a Gradient Nanostructured Austenite Stainless Steel

Thermal relaxation of compressive residual stresses in surface gradient nanostructure of TC11 titanium alloy

The Effect of Stress Gradient on the Formation of TCP Phases in a Ni-based Single Crystal Superalloy at 1050 Oc

In Situ Heating Neutron and X‐Ray Diffraction Analyses for Revealing Structural Evolution during Postprinting Treatments of Additive‐Manufactured 316L Stainless Steel

High-temperature fatigue behavior and cyclic deformation of a gradient nanostructured RAFM steel

Influences of Nano-structured Thermal Stability on the Intergranular Corrosion of High-Carbon Austenitic Heat-Resistant Steel

In-Situ Synchrotron HEXRD Study on the Micro-Stress Evolution Behavior of a Superalloy During Room-Temperature Compression

Gradient Nanostructure and Residual Stresses Induced by Ultrasonic Nano-Crystal Surface Modification in 304 Austenitic Stainless Steel for High Strength and High Ductility

Residual Stress Modeling and Advanced Diffraction Measurements of 347H Steel Weldments

Research on Multi-Scale Failure Mechanism of Gradient Nanostructured 316L Steel under Strain-Controlled Fatigue at 650 °C

Unravelling thermal history during additive manufacturing of martensitic stainless steel

Inhibition of Intergranular Corrosion in Austenitic Stainless Steels Through Critical Near-Surface Plastic Deformation and Aging

Identifying Multiple Synergistic Factors on the Susceptibility to Stress Relaxation Cracking in Variously Heat-Treated Weldments

Abnormal Grain Growth Behavior in Gradient Nanostructured Titanium Investigated by Coupled Quasi-in-situ EBSD Experiments and Phase-Field Simulations

Study on the Mechanical Stability of Reversed Austenite in Super Martensitic Stainless Steel Via In-Situ Synchrotron High Energy X-ray Diffraction

An Investigation into the Effect of Stress on the Formation and Stability of Carbon S-Phase on Austenitic Stainless Steel

Intergranular precipitation behavior and its influence on the stress relaxation cracking susceptibility of Super304H austenitic stainless steel weld metal during long-term aging

Mechanism of stress relaxation and phase transformation in additively manufactured Ti-6Al-4V via in situ high temperature XRD and TEM analyses

Thermomechanical processing model and abnormal microstructure evolution of high-nitrogen stainless steel X30CrMoN15-1