Thermal deformation behavior and microstructure analysis of the as-cast super austenitic stainless steel Sanicro35

Yang Li,Min Li,Guang hui Zhao,Yinghui Wei

DOI: https://doi.org/10.1088/2053-1591/ad33d8

IF: 2.025

2024-03-15

Materials Research Express

Abstract:Uniaxial thermal compression of the super austenitic stainless steel Sanicro35. The thermal deformation behavior was investigated under the conditions of 900~1150 °C deformation temperature and 0.001~10 s-1 strain rate. The microstructure of the large deformation zone of the specimen was investigated using electron backscatter diffraction (EBSD). The results show that the thermal compression rheological stress of the super austenitic stainless steel Sanicro 35 decreases with increasing temperature and decreasing strain rate. Dynamic recrystallization (DRX) is the main softening mechanism for this material. The analysis of the microstructure by EBSD on the morphological features, recrystallization fraction, dislocation density and twin boundary distribution can be found that the higher grain boundary mobility drives the DRX grains to grow with the deformation temperature increases. As the strain rate increases, the larger deformation storage energy provides sufficient activation energy for DRX grain nucleation, and the nucleation of DRX grains becomes denser. The twin boundaries are mainly distributed within the DRX grains. The smaller the grain size of DRX, the denser the nucleation of twin boundaries, and the generation of twins can promote the development of DRX. The softening mechanism under most deformation conditions is discontinuous dynamic recrystallization (DDRX). However, at a strain rate of 10 s-1, the high strain rate causes microbands to be generated within the deformed grains, and the microband boundaries evolve toward the high-angle grain boundaries (HAGBs) with increasing temperature, which promotes the occurrence of Continuous dynamic recrystallization (CDRX), and the dynamic softening mechanism is the coexistence of DDRX and CDRX. The results of the study show that the reasonable hot working deformation region is: temperature of 1050-1150 °C and strain rate of 10 s-1.

materials science, multidisciplinary