Research on Microstructural Evolution and Deformation Mechanisms in SCM435 Steel Based on a Dynamic Material Model

Tongyao Yang,Zhongze Du,Zejiang Qi,Qingjuan Wang,Zhao Zhang,Wang, Qingjuan

DOI: https://doi.org/10.1007/s11837-024-06454-0

2024-03-07

JOM

Abstract:This paper utilizes the dynamic material model (DMM) to construct a hot working diagram, investigating the microstructural evolution within the deformation zone in the temperature range of 750–1100°C and strain rate range of 0.1–20 s −1 . The hot working diagram delineates the stable processing zone and the rheological instability zone, with distinct processing parameters leading to varied internal deformation mechanisms. The high-power dissipation zone ( η ≥ 0.3) represents a stable processing area where the dominant deformation mechanism is dynamic recrystallization (DRX), occurring at a deformation temperature of 980–1100°C and a strain rate of 0.1–5 s −1 . Higher temperatures and lower strain rates facilitate the nucleation of DRX, resulting in a microstructure characterized by complete DRX grains. Moreover, increasing deformation temperature and decreasing strain rate lead to larger DRX grain sizes. In the temperature range of 900–980°C and across all strain rates, the medium power dissipation zone (0.2 ≤ η < 0.3) exhibits a deformation mechanism resulting from the combined effects of dynamic recovery (DRV) and DRX. Numerous small grains initiate at the initial grain boundaries, forming a necklace structure wherein sawtooth or protruding grain boundaries indicate the initiation of DRX. Within the rheological instability zone ( η < 0.2), characterized by temperatures below 900°C, the microstructure is comprised of elongated deformed grains accompanied by localized shear bands along the grain boundaries.

materials science, multidisciplinary,metallurgy & metallurgical engineering,mining & mineral processing,mineralogy