Abstract:Laser shock peening (LSP) can induce the compressive residual stress (CRS) on the surface of the material, and surface nanocrystallization can be realized with a nanocrystal layer, thereby significantly improving the high-cycle fatigue performance. However, due to weak material constrain and the high working temperature of thin aero-engine compressor blades, CRS and refined grain structure are more likely to result in stress relaxation and microstructural recovery under thermal stress load, resulting in reducing the anti-fatigue effect of LSP. In this paper, on the basis of the surface nanocrystallization induced by LSP, residual stress and microstructure of TC11 titanium alloy thin components were measured and observed. The residual stress relaxation was characterized and the microstructure evolution was discussed. Also, the thermal stability mechanism of CRS and the nanostructure on the surface were analyzed. The experimental results show that after thermal loads, the CRS was decreased, and the stress relaxation amplitude was increased with an increase in temperature. After annealing at 400 degrees C, the dislocation density was significantly reduced, but the grain sizes of surface nanostructure did not greatly increase. After annealing at 400 degrees C for 2 h, the fatigue strength of the LSPed specimen was reduced compared with that before annealing, but it was still increased compared with the original state without LSP, especially under high-power density for multiple LSP treatment. It can be concluded that the surface nanostructure has good stability and effectively retards the initiation of fatigue cracks on the surface, which ensures the effectiveness of LSP under thermal loads. (c) 2022 Author(s). All article content, except where otherwise noted, is licensed under a Creative Commons Attribution (CC BY) license (http://creativecommons.org/licenses/by/4.0/).

Thermal relaxation of compressive residual stresses in surface gradient nanostructure of TC11 titanium alloy

Strain-induced Refinement and Thermal Stability of a Nanocrystalline Steel Produced by Surface Mechanical Attritiontreatment

In-situ Investigation Via High Energy X-ray Diffraction of Stress-Induced(0002)α→(110)β Transformation in a Ti-5.5Mo-7.2Al-4.5Zr-2.6Sn-2.1Cr Alloy

Thermal stability study of TC11 titanium alloy thin component after surface nanocrystallization induced by laser shock processing

Effect of Contact Stress and Slip Amplitude on Fretting Fatigue Behaviour of Ultrasonic Surface Nanocrystallized TC11 Titanium Alloy

Investigation of thermal stability of residual stresses and microstructure of dual shot peened TC17 titanium alloy

Effect of grain size on high-temperature stress relaxation behavior of fine-grained TC4 titanium alloy

Effect of Thermal Annealing on the Microstructure, Mechanical Properties and Residual Stress Relaxation of Pure Titanium after Deep Rolling Treatment

Stability of Residual Stresses in Ultrasonic Surface Deep Rolling Treated Ti-6Al-4V Alloy under Cyclic Loading

Relaxation mechanisms of near – α titanium alloy during stress relaxation with synchronous aging

Deformation-induced Ambient Temperature A-to-ß Phase Transition and Nanocrystallization in (α + SS) Titanium Alloy

Microstructure and Texture Evolution in a Post-dynamic Recrystallized Titanium During Annealing, Monotonic and Cyclic Loading

Deformation Mechanism and In-Situ TEM Compression Behavior of TB8 Β Titanium Alloy with Gradient Structure

Correlation between Precipitation and Recrystallisation during Stress Relaxation in Titanium Microalloyed Steel

Simulated and Experimental Investigation on Discontinuous Dynamic Recrystallization of a Near-Α TA15 Titanium Alloy During Isothermal Hot Compression in Β Single-Phase Field

Cold creep of titanium: Analysis of stress relaxation using synchrotron diffraction and crystal plasticity simulations

7075 aluminum alloy induced by ultrasonic surface rolling: grain refinement and residual stress model analysis and evaluation

Thermal Stability and Microstructure Evolution in Nanocrystalline Ti-5Al-2Sn-2Zr-4Mo-4Cr – A HRTEM Study

Face-centered Titanium Induced by Ultrasonic Surface Rolling Process in Ti-6Al-4V Alloy and Its Tensile Behavior

Residual Stress and Microstructure of Ti6Al4V Treated by Thermal-Vibratory Stress Relief Process

Strain Rate Dependence and Recrystallization Modeling for TC18 Alloy During Post-Deformation Annealing