Abstract:In this study, equal channel angular pressing (ECAP) was applied to a hot-extruded Mg–5.00Zn–0.92Y–0.16Zr (wt.%) alloy to produce an ultrafine-grained a-Mg structure of 0.6μm with uniformly distributed fine quasicrystal Mg3YZn6 particles. The basal planes in the as-ECAPed alloy were inclined approximately 45° to the ECAP direction (EPD); thus, a high Schmid factor of 0.36 for (0001)〈112¯0〉 basal slip along EPD was obtained. Then, the superplastic behavior at low temperatures of 150–250°C and initial strain rates of 1.67×10−3s−1–1.67×10−1s−1 of the as-ECAPed alloy was investigated and compared with that of the as-extruded alloy. The microstructural development, texture evolution and cracking behavior during tensile tests were systemically investigated by electron backscattered diffraction (EBSD) analysis. During the tensile test along the EPD, the basal planes in the as-ECAPed alloy specimen were tilted approximately 15° away from the original position; thus, the basal planes were still in a position favorable for the basal slip along the EPD. As a result, a maximum elongation of 865% was obtained at 200°C and a strain rate of 1.67×10−3s−1, as a result of this favored basal texture and the excellent thermal stability of the ultrafine-grained structure. This optimum superplastic temperature of 200°C is much lower than that obtained for other Mg–Zn–Y–(Zr) alloys. In contrast, for the as-extruded alloy specimen, superplastic behavior did not occur until the critical condition of 250°C and a strain rate of 1.67×10−3s−1. Below this temperature and strain rate, the strong extrusion basal texture was maintained, and the cracks in the hot-worked coarse region (or un-DRXed region) were observed nucleating mainly associated with the formation of a 38° {101¯1}–{101¯2} double twin. At this temperature and strain rate, the hot-worked coarse regions were significantly refined by the dynamic recovery and the following recrystallization process. In the case, the formation of a double twin was prevented and the facture was delayed.

Superplastic Behaviors of a Mg–Zn–Y–Zr Alloy Processed by Extrusion and Equal Channel Angular Extrusion

Superplastic Behavior of an Extruded Mg-Zn-Y-Zr Alloy

A Comparative Study on Superplasticity of Mg-Zn-Y-Zr Processed by Ecae and Hot Rolling

The Microstructural Evolution and Superplastic Behavior at Low Temperatures of Mg–5.00Zn–0.92Y–0.16Zr (wt.%) Alloys after Hot Extrusion and ECAP Process

Superplasticity of Mg-5.8Zn-1Y-Zr Alloy Sheet Fabricated by Combination of Extrusion and Hot-Rolling Processes

Achieving High Strain Rate Superplasticity in Mg–Y–Nd–Zr Alloy Processed by Homogenization Treatment and Equal Channel Angular Pressing

Enhancement of Superplasticity in a Fine-Grained Mg–3Gd–1Zn Alloy Processed by Equal-Channel Angular Pressing

Superplastic Behavior and Microstructure Evolution of a Fine-Grained Mg-Nd-Zn-Zr Alloy Processed by Hot Extrusion

Microstructural Evolution and Enhanced Superplasticity in Friction Stir Processed Mg–Zn–Y–Zr Alloy

Microstructural Evolution of a Fine-Grained Mg-Y-Nd Alloy During Superplastic Deformation

Superplastic Behavior and Microstructure Evolution of A New Al-Mg-Sc-Zr Alloy Subjected to A Simple Thermomechanical Processing

Superplasticity and Microstructure in Mg–Gd–Y–Zr Alloy Prepared by Extrusion

Realizing impressive superplasticity in a low-alloyed Mg-Zn-Ca-Al-Mn alloy: The roles of grain boundary segregation and dense β-Mn particles

Superplasticity in Mg–Li–Zn Alloys Processed by High Ratio Extrusion

Superplasticity of Mg–Zn–Y Alloy Containing Quasicrystal Phase Processed by Equal Channel Angular Pressing

Superplastic Behavior and Microstructure Evolution of a Fine-Grained Mg–Y–Nd Alloy Processed by Submerged Friction Stir Processing

Effect of equal channel angular extrusion process on deformation behaviors of Mg-3Al-Zn alloy

Superplastic Behavior and Microstructural Evolution in a Commercial Mg-3Al-1Zn Magnesium Alloy.

On Mechanical Properties and Superplasticity of Mg–15Al–1Zn Alloys Processed by Reciprocating Extrusion

Dynamic Compressive Behaviour and Microstructural Evolution of Extrusion-Shear Mg–6Zn–1Cu–1Y–0.6Zr Alloy

Achieving High Superplasticity of a New Al–Mg–Sc–Zr Alloy Sheet Prepared by a Simple Thermal–mechanical Process