Effect Cf Nano-ZnO or Nano-Y 2 O 3 on Sintering Property of Fused Quartz Ceramics

 Bu,Jinglong,Guihai Chen,Yuejun,Anchi Yu,Lixue,Hong Wang,Zhifa

2014-01-01

Abstract:Fused quartz ceramic was prepared using high purity fused quartz powder as starting material,separately introducing 1%,2% and 3%( in mass,the same hereinafter) nano-ZnO or nano-Y2O3as additive,molding at 50 MPa, firing in reduction atmosphere at1 300,1 350 and 1 400 ℃ for 1 h,respectively. Apparent porosity and cold modulus of rupture were tested and fracture morphology was analyzed by SEM. The results show that adding nano-ZnO or nano-Y2O3obviously improves sintering of fused quartz; adding nano-ZnO enhances modulus of rupture and decreases apparent porosity; the optimum addition of nano-Y2O3as sintering aid of fused quartz is 2%.